ACRYLITE® Hi-Gloss NTA-5
聚甲基丙烯酸甲酯-丙烯酸
ACRYLITE® Hi-Gloss NTA-5 black is an amorphous thermoplastic molding compound, based on impact-modified polymethyl methacrylate (PMMA).
Properties
ACRYLITE® molding compounds have the following typical properties:
ACRYLITE® Hi-Gloss NTA-5 black is characterized by the following additional properties:
Application areas are:
Add-on automotive body parts, pillar-trims, mirror housings, trim parts at front - and rear end, etc.
添加剂 | |
特性 | - 冲击改性、高光、高强度、抗撞击性高、可回收材料、耐气候影响性能良好、无定形的
|
用途 | |
机构评级 | |
外观 | |
形式 | |
加工方法 | |
密度 | 1.16 | g/cm³ | ISO 1183 |
熔融体积流量（MVR） |
|
| ISO 1133 |
230°C/3.8 kg | 0.0793 | in³/10min |
|
260°C/3.8 kg | 0.488 | in³/10min |
|
吸水率 |
|
| ISO 62 |
饱和, 73°F | 1.5 | % |
|
平衡, 73°F, 50% RH | 0.50 | % |
|
拉伸模量 | 305000 | psi | ISO 527-2/1 |
拉伸应力 (屈服) | 7830 | psi | ISO 527-2/50 |
拉伸应变 (屈服) | 5.0 | % | ISO 527-2/50 |
标称拉伸断裂应变 | 48 | % | ISO 527-2 |
简支梁无缺口冲击强度 (73°F) | 52 | ft·lb/in² | ISO 179/1eU |
热变形温度 |
|
|
|
66 psi, 未退火 | 216 | °F | ISO 75-2/B |
264 psi, 未退火 | 205 | °F | ISO 75-2/A |
玻璃转化温度 | 235 | °F | ISO 11357-2 |
维卡软化温度 | 217 | °F | ISO 306/B50 |
线形热膨胀系数 - 流动 (32 到 122°F) | 6.1E-5 | in/in/°F | ISO 11359-2 |
UL 阻燃等级 (0.06 in) | HB |
| IEC 707 |
干燥温度 | 176 | °F |
|
干燥时间 | > 4.0 | hr |
|
加工（熔体）温度 | 446 到 500 | °F |
|
模具温度 | 140 到 176 | °F |
|