RTP ESD C 201
聚酰胺66
Warning: The status of this material is 'Commercial: Limited Issue'
The data for this material has not been recently verified.
Please contact RTP Company for current information prior to specifying this grade.
填料/增强材料 | |
添加剂 | |
特性 | |
机构评级 | |
RoHS 合规性 | |
外观 | |
形式 | |
加工方法 | |
密度 / 比重 | 1.24 |
| ASTM D792 |
收缩率 - 流动 (0.125 in) | 7.0E-3 到 9.0E-3 | in/in | ASTM D955 |
吸水率 (24 hr, 73°F) | 1.0 | % | ASTM D570 |
拉伸模量 | 570000 | psi | ASTM D638 |
抗张强度 | 9000 | psi | ASTM D638 |
伸长率 (断裂) | 3.0 | % | ASTM D638 |
弯曲模量 | 520000 | psi | ASTM D790 |
弯曲强度 | 14000 | psi | ASTM D790 |
悬壁梁缺口冲击强度 (0.125 in) | 1.5 | ft·lb/in | ASTM D256 |
无缺口悬臂梁冲击 (0.125 in) | 8.0 | ft·lb/in | ASTM D4812 |
载荷下热变形温度 |
|
| ASTM D648 |
66 psi, 未退火 | 420 | °F |
|
264 psi, 未退火 | 370 | °F |
|
线形热膨胀系数 - 流动 | 2.4E-5 | in/in/°F | ASTM D696 |
表面电阻率 | 1.0E+6 | ohms | ASTM D257 |
体积电阻率 | 1.0E+3 | ohms·cm | ASTM D257 |
UL 阻燃等级 (0.06 in, RTP Tested) | HB |
| UL 94 |
Tensile Elongation, ASTM D638: 3-6%
Volume Resistivity, ASTM D257: <10E3 ohm-cm
Surface Resistivity, ASTM D257: <10E6 ohm/sq
Static Decay, FTMS-4046.1, Mil B-81705C: <2.0 seconds |
料筒后部温度 | 525 到 550 | °F |
|
料筒中部温度 | 525 到 550 | °F |
|
料筒前部温度 | 525 到 550 | °F |
|
模具温度 | 150 到 225 | °F |
|
注塑压力 | 12000 到 18000 | psi |
|
如需安特普原厂物性表及相关文件，请联系我们工作人员，谢谢！