Ixef® FC-1022

Ixef® FC-1022

产品产商:索尔维(SOLVAY)
产品产地:进口/中国
产品类别:IXEF PARA
产品型号:Ixef FC-1022
产品规格:25KG/包
产品特性:超强刚性,尺寸稳定性良好,出色的外观,低吸湿性,高强度,好的消毒性,良好的抗蠕变性,流动性高,耐化学性良好,食品接触,合规性,通用

Ixef® FC-1022

聚丙烯酰胺
产品说明:
Ixef® FC-1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound that exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance.

Ixef® FC-1022 is approved for food contact and meets FDA regulations for Ixef® FC-1022 NT 000 (natural) and Ixef® FC-1022 BK 001 (black) based on clearances granted by FCN 001242 for repeated use food contact applications with all food types, under FDA conditions of use B through H as described in Tables 1 and 2 of 21 CFR 176.170(c).

  • Black: FC-1022 BK 001

  • Natural: FC-1022 NT 000


填料/增强材料
  • 玻璃纤维增强材料, 50% 填料按重量

特性
  • 超强刚性,尺寸稳定性良好,出色的外观,低吸湿性,高强度,好的消毒性,良好的抗蠕变性,流动性高,耐化学性良好,食品接触的合规性,通用
用途
  • 电器用具,高光应用,食品服务领域,医疗器材
机构评级
  • FDA 21 CFR 176.170(c) 3NSF 51 4欧洲 10/1/2011 12:00:00 AM
RoHS 合规性
  • RoHS 合规

外观
  • 黑色,自然色
形式
  • 粒子

加工方法
  • 注射成型

物理性能
干燥
调节后的
单位制
测试方法
密度
1.64
--
g/cm³
ISO 1183
收缩率
0.10 到 0.30
--
%
ISO 294-4
吸水率 (73°F, 24 hr)
0.16
--
%
ISO 62
机械性能
干燥
调节后的
单位制
测试方法
拉伸模量
2.83E+6
2.83E+6
psi
ISO 527-2
拉伸应力 (断裂)
40600
37700
psi
ISO 527-2
拉伸应变 (断裂)
1.9
2.2
%
ISO 527-2
弯曲模量
2.68E+6
--
psi
ISO 178
弯曲应力
55100
--
psi
ISO 178
冲击性能
干燥
调节后的
单位制
测试方法
悬壁梁缺口冲击强度
2.1
--
ft·lb/in
ASTM D256
无缺口悬臂梁冲击
16
--
ft·lb/in
ASTM D256
热性能
干燥
调节后的
单位制
测试方法
热变形温度 (264 psi, 未退火)
446
--
°F
ISO 75-2/A
线形热膨胀系数 - 流动
8.3E-6
--
in/in/°F
ISO 11359-2
补充信息
干燥
调节后的


吸水性 - Equil, 65% RH
--



注射
干燥
单位制

干燥温度
248
°F

干燥时间
0.50 到 1.5
hr

料筒后部温度
482 到 500
°F

料筒前部温度
500 到 554
°F

射嘴温度
500 到 554
°F

加工(熔体)温度
536
°F

模具温度
248 到 284
°F

注射速度
快速


注射说明
Hot runners: 250°C to 260°C (482°C to 500°F)

Storage
Ixef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Ixef® processing guide.

Drying
The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F).

Injection Molding
Ixef® FC-1022 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure.

The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260 to 290°C (500 to 554°F) in the front zone. If hot runners are used, they should be set to 250 to 260°C (482 to 500°F).

To maximize crystallinity, the temperature of the mold cavity surface must be held between 120 and 140°C (248 and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%).