CYCOLAC™ Resin FR15
丙烯腈丁二烯苯乙烯
产品说明:
Flame retardant ABS (non-PBBE additive). Good property/toughness. Excellent moldability. UL94 V-0/5VA rated.
添加剂 | |
特性 | |
加工方法 | |
多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Flexural DMA (ASTM D4065) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)
|
密度 / 比重 |
|
|
|
-- | 1.20 |
| ASTM D792 |
-- | 1.19 | g/cm³ | ISO 1183 |
熔流率（熔体流动速率） |
|
|
|
230°C/3.8 kg | 4.0 | g/10 min | ASTM D1238 |
220°C/5.0 kg | 10 | g/10 min | ISO 1133 |
收缩率 - 流动 (0.126 in) | 5.0E-3 到 7.0E-3 | in/in | 内部方法 |
拉伸模量 3 | 340000 | psi | ASTM D638 |
抗张强度 |
|
|
|
屈服 4 | 6000 | psi | ASTM D638 |
屈服 | 5980 | psi | ISO 527-2/50 |
断裂 4 | 5100 | psi | ASTM D638 |
断裂 | 4540 | psi | ISO 527-2/50 |
伸长率 |
|
|
|
屈服 4 | 2.3 | % | ASTM D638 |
屈服 | 2.1 | % | ISO 527-2/50 |
断裂 4 | 9.0 | % | ASTM D638 |
断裂 | 34 | % | ISO 527-2/50 |
弯曲模量 5 (1.97 in 跨距) | 395000 | psi | ASTM D790 |
弯曲强度 5 (屈服, 1.97 in 跨距) | 10400 | psi | ASTM D790 |
简支梁缺口冲击强度 6 (73°F) | 9.3 | ft·lb/in² | ISO 179/1eA |
悬壁梁缺口冲击强度 |
|
|
|
73°F | 4.0 | ft·lb/in | ASTM D256 |
-22°F 7 | 3.1 | ft·lb/in² | ISO 180/1A |
73°F 7 | 8.9 | ft·lb/in² | ISO 180/1A |
装有测量仪表的落镖冲击 (73°F, Total Energy) | 300 | in·lb | ASTM D3763 |
载荷下热变形温度 |
|
|
|
66 psi, 未退火, 0.126 in | 180 | °F | ASTM D648 |
264 psi, 未退火, 0.126 in | 158 | °F | ASTM D648 |
264 psi, 未退火, 2.52 in 跨距 8 | 164 | °F | ISO 75-2/Af |
维卡软化温度 |
|
|
|
-- | 187 | °F | ASTM D1525 9 |
-- | 178 | °F | ISO 306/B50 |
-- | 183 | °F | ISO 306/B120 |
线形热膨胀系数 |
|
| ASTM E831 |
流动 : -40 到 104°F | 4.7E-5 | in/in/°F |
|
横向 : -40 到 104°F | 4.8E-5 | in/in/°F |
|
RTI Elec | 140 | °F | UL 746 |
RTI Imp | 140 | °F | UL 746 |
RTI | 140 | °F | UL 746 |
耐电弧性 10 | PLC 7 |
| ASTM D495 |
相比耐漏电起痕指数(CTI) | PLC 2 |
| UL 746 |
高电弧燃烧指数(HAI) | PLC 4 |
| UL 746 |
高电压电弧起痕速率 (HVTR) | PLC 4 |
| UL 746 |
热丝引燃 (HWI) | PLC 3 |
| UL 746 |
UL 阻燃等级 |
|
| UL 94 |
0.06 in | V-0 |
|
|
0.10 in | 5VA |
|
|
熔体粘度 (392°F, 1000 sec^-1) | 290 | Pa·s | ASTM D3835 |
干燥温度 | 180 到 190 | °F |
|
干燥时间 | 2.0 到 4.0 | hr |
|
干燥时间，最大 | 6.0 | hr |
|
建议的最大水分含量 | 0.10 | % |
|
建议注射量 | 50 到 70 | % |
|
料筒后部温度 | 340 到 360 | °F |
|
料筒中部温度 | 380 到 400 | °F |
|
料筒前部温度 | 390 到 420 | °F |
|
射嘴温度 | 390 到 430 | °F |
|
加工（熔体）温度 | 390 到 430 | °F |
|
模具温度 | 120 到 160 | °F |
|
背压 | 50.0 到 100 | psi |
|
螺杆转速 | 30 到 60 | rpm |
|
排气孔深度 | 1.5E-3 到 2.0E-3 | in |
|
如需沙伯基础（SABIC）原厂物性表及相关文件，请联系我们工作人员，谢谢！