CYCOLAC™ Resin EX58
丙烯腈丁二烯苯乙烯
产品说明:
High impact ABS for sheet extrusion and blow molding applications.
密度 / 比重 |
|
|
|
-- | 1.03 |
| ASTM D792 |
-- | 1.03 | g/cm³ | ISO 1183 |
熔流率(熔体流动速率) (220°C/10.0 kg) | 4.0 | g/10 min | ISO 1133 |
收缩率 - 流动 (0.126 in) | 6.0E-3 到 8.0E-3 | in/in | 内部方法 |
洛氏硬度 (R 级) | 102 |
| ASTM D785 |
拉伸模量 |
|
|
|
-- 2 | 302000 | psi | ASTM D638 |
-- | 286000 | psi | ISO 527-2/1 |
抗张强度 |
|
|
|
屈服 3 | 5660 | psi | ASTM D638 |
屈服 | 5950 | psi | ISO 527-2/50 |
断裂 3 | 4350 | psi | ASTM D638 |
断裂 | 4350 | psi | ISO 527-2/50 |
伸长率 |
|
|
|
屈服 3 | 3.1 | % | ASTM D638 |
屈服 | 2.6 | % | ISO 527-2/50 |
断裂 3 | 32 | % | ASTM D638 |
断裂 | 21 | % | ISO 527-2/50 |
弯曲模量 |
|
|
|
1.97 in 跨距 4 | 313000 | psi | ASTM D790 |
-- 5 | 290000 | psi | ISO 178 |
弯曲应力 |
|
|
|
-- 5, 6 | 8700 | psi | ISO 178 |
屈服, 1.97 in 跨距 4 | 9570 | psi | ASTM D790 |
简支梁缺口冲击强度 7 (73°F) | 18 | ft·lb/in² | ISO 179/1eA |
悬壁梁缺口冲击强度 |
|
|
|
-22°F | 5.6 | ft·lb/in | ASTM D256 |
73°F | 8.1 | ft·lb/in | ASTM D256 |
-22°F 8 | 11 | ft·lb/in² | ISO 180/1A |
73°F 8 | 17 | ft·lb/in² | ISO 180/1A |
装有测量仪表的落镖冲击 (73°F, Total Energy) | 327 | in·lb | ASTM D3763 |
载荷下热变形温度 |
|
|
|
66 psi, 未退火, 0.126 in | 196 | °F | ASTM D648 |
264 psi, 未退火, 0.126 in | 169 | °F | ASTM D648 |
264 psi, 未退火, 2.52 in 跨距 9 | 172 | °F | ISO 75-2/Af |
维卡软化温度 |
|
|
|
-- | 223 | °F | ASTM D1525 10 |
-- | 203 | °F | ISO 306/B50 |
-- | 207 | °F | ISO 306/B120 |
线形热膨胀系数 |
|
| ASTM E831 |
流动 : -40 到 104°F | 5.6E-5 | in/in/°F |
|
横向 : -40 到 104°F | 5.8E-5 | in/in/°F |
|
RTI Elec | 140 | °F | UL 746 |
RTI Imp | 140 | °F | UL 746 |
RTI | 140 | °F | UL 746 |
耐电弧性 11 | PLC 5 |
| ASTM D495 |
相比耐漏电起痕指数(CTI) | PLC 0 |
| UL 746 |
高电弧燃烧指数(HAI) | PLC 4 |
| UL 746 |
高电压电弧起痕速率 (HVTR) | PLC 1 |
| UL 746 |
热丝引燃 (HWI) | PLC 4 |
| UL 746 |
UL 阻燃等级 (0.06 in) | HB |
| UL 94 |
熔体粘度 (464°F, 100 sec^-1) | 1550 | Pa·s | ASTM D3835 |
Extrusion Blow Molding Parameters: Sheet Extrusion Parameters: |