Elastollan® SP 9322
热塑性聚氨酯弹性体（聚酯）
产品说明:
Thermoplastic Polyester-Polyurethane Compound with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping characteristic and high resilience performance, phthalatfree.
密度 | 1.16 | g/cm³ | ISO 1183/A |
肖氏硬度 (邵氏 A, 3 秒) | 52 |
| ISO 7619 |
磨损量 | 120 | mm³ | ISO 4649-A |
拉伸应力 |
|
| DIN 53504-S2 |
20%应变 | 102 | psi |
|
100%应变 | 261 | psi |
|
300%应变 | 667 | psi |
|
抗张强度 | 3630 | psi | DIN 53504-S2 |
伸长率 (断裂) | 900 | % | DIN 53504-S2 |
撕裂强度 2 | 200 | lbf/in | ISO 34-1 |
压缩永久变形 |
|
| ISO 815 |
73°F, 72 hr | 25 | % |
|
158°F, 24 hr | 38 | % |
|
212°F, 24 hr | 53 | % |
|
The plaques are manufactured by injection moulding from pre-dried granules (water content less 0,02%). Test paques are aged 20 hrs at 100°C.
Specimens are cut from test plaques. The test conditions: 23°C ± 2°C and 50% ± 6% rel. humidity. |
干燥温度 | 176 到 194 | °F |
|
干燥时间 | 2.0 到 3.0 | hr |
|
建议的最大水分含量 | 0.020 | % |
|
料筒后部温度 | 356 到 392 | °F |
|
料筒中部温度 | 365 到 410 | °F |
|
料筒前部温度 | 374 到 410 | °F |
|
加工（熔体）温度 | 374 到 410 | °F |
|
模具温度 | 68 到 104 | °F |
|
注射速度 | 慢 |
|
|
如需巴斯夫原厂物性表及相关文件，请联系我们工作人员，谢谢！