Elastollan® C90A
热塑性聚氨酯弹性体（聚酯）
产品说明:
Elastollan® C90A exhibits excellent abrasion resistance and toughness, good hydrolytic stability, good heat, oil, fuel and solvent resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® C90A is supplied uncolored in pellet form.
密度 / 比重 | 1.21 |
| ASTM D792 |
熔流率（熔体流动速率） (210°C/21.6 kg) | 30 到 50 | g/10 min | ASTM D1238 |
肖氏硬度 (邵氏 A) | 90 |
| ASTM D2240 |
拉伸模量 (注塑) | 5700 | psi | ASTM D412 |
弯曲模量 (注塑) | 7000 | psi | ASTM D790 |
泰伯耐磨性 | 25.0 | mg | ASTM D1044 |
Abrasion - DIN | 25 | mm³ | DIN 53516 |
拉伸应力 |
|
| ASTM D412 |
100%应变 | 1500 | psi |
|
300%应变 | 3300 | psi |
|
抗张强度 | 6400 | psi | ASTM D412 |
伸长率 (断裂) | 520 | % | ASTM D412 |
撕裂强度 2 | 760 | lbf/in | ASTM D624 |
压缩永久变形 |
|
| ASTM D395B |
73°F, 22 hr | 25 | % |
|
158°F, 22 hr | 40 | % |
|
玻璃转化温度 | -36.4 | °F | 内部方法 |
维卡软化温度 | 262 | °F | ASTM D1525 |
Softening Point - DMA | 235 | °F | 内部方法 |
干燥温度 | 212 到 230 | °F |
|
干燥时间 | 2.0 到 3.0 | hr |
|
建议的最大水分含量 | 0.030 | % |
|
料筒后部温度 | 374 到 428 | °F |
|
料筒中部温度 | 374 到 428 | °F |
|
料筒前部温度 | 374 到 428 | °F |
|
射嘴温度 | 410 到 437 | °F |
|
干燥温度 | 212 到 230 | °F |
|
干燥时间 | 2.0 到 3.0 | hr |
|
料筒1区温度 | 338 到 410 | °F |
|
料筒3区温度 | 338 到 410 | °F |
|
料筒5区温度 | 338 到 410 | °F |
|
接头温度 | 392 到 428 | °F |
|
口模温度 | 383 到 419 | °F |
|
如需巴斯夫原厂物性表及相关文件，请联系我们工作人员，谢谢！