Elastollan® C60AW
热塑性聚氨酯弹性体（聚酯）
产品说明:
Elastollan® C60AW is a polyester-based thermoplastic polyurethane (TPU) containing a plasticizer. It exhibits excellent abrasion resistance and toughness, good hydrolytic stability, good heat, oil, fuel and solvent resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® C60AW is supplied uncolored in pellet form.
密度 / 比重 | 1.14 |
| ASTM D792 |
熔流率（熔体流动速率） (190°C/3.8 kg) | 20 到 60 | g/10 min | ASTM D1238 |
肖氏硬度 (邵氏 A) | 61 |
| ASTM D2240 |
拉伸模量 (注塑) | 800 | psi | ASTM D412 |
弯曲模量 (注塑) | 1300 | psi | ASTM D790 |
泰伯耐磨性 | 40.0 | mg | ASTM D1044 |
Abrasion - DIN | 20 | mm³ | DIN 53516 |
拉伸应力 |
|
| ASTM D412 |
100%应变 | 530 | psi |
|
300%应变 | 1300 | psi |
|
抗张强度 | 3400 | psi | ASTM D412 |
伸长率 (断裂) | 760 | % | ASTM D412 |
撕裂强度 2 | 370 | lbf/in | ASTM D624 |
压缩永久变形 |
|
| ASTM D395B |
73°F, 22 hr | 20 | % |
|
158°F, 22 hr | 45 | % |
|
玻璃转化温度 | -61.6 | °F | 内部方法 |
维卡软化温度 | 151 | °F | ASTM D1525 |
Softening Point - DMA | 228 | °F | 内部方法 |
建议的最大水分含量 | 0.030 | % |
|
料筒后部温度 | 338 到 410 | °F |
|
料筒中部温度 | 338 到 410 | °F |
|
料筒前部温度 | 338 到 410 | °F |
|
射嘴温度 | 392 到 410 | °F |
|
料筒1区温度 | 284 到 347 | °F |
|
料筒3区温度 | 284 到 347 | °F |
|
料筒5区温度 | 284 到 347 | °F |
|
接头温度 | 320 到 347 | °F |
|
口模温度 | 329 到 338 | °F |
|
如需巴斯夫原厂物性表及相关文件，请联系我们工作人员，谢谢！