Elastollan® 890AN
热塑性聚氨酯弹性体（聚酯）
产品说明:
Elastollan® 890AN is specifically formulated for transparent film applications. It exhibits excellent abrasion resistance, toughness, transparency, and oil/fuel resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan®890AN conforms to the FDA food contact regulations as described in book 21, section 177.2600 and 177.1680 for both wet and dry food contact applications respectively. Elastollan® 890AN is supplied uncolored in pellet form.
机构评级 | FDA 21 CFR 177.1680、FDA 21 CFR 177.2600 |
外观 | |
加工方法 | 挤出、注射成型 |
密度 / 比重 | 1.22 |
| ASTM D792 |
熔流率（熔体流动速率） (190°C/8.7 kg) | 15 到 30 | g/10 min | ASTM D1238 |
肖氏硬度 (邵氏 A) | 92 |
| ASTM D2240 |
拉伸模量 (注塑) | 4200 | psi | ASTM D412 |
弯曲模量 (注塑) | 9700 | psi | ASTM D790 |
泰伯耐磨性 | 45.0 | mg | ASTM D1044 |
Abrasion - DIN | 25 | mm³ | DIN 53516 |
拉伸应力 |
|
| ASTM D412 |
100%应变 | 2000 | psi |
|
300%应变 | 4500 | psi |
|
抗张强度 | 5700 | psi | ASTM D412 |
伸长率 (断裂) | 480 | % | ASTM D412 |
撕裂强度 2 | 820 | lbf/in | ASTM D624 |
压缩永久变形 |
|
| ASTM D395B |
73°F, 22 hr | 20 | % |
|
158°F, 22 hr | 45 | % |
|
玻璃转化温度 | 6.80 | °F | 内部方法 |
维卡软化温度 | 248 | °F | ASTM D1525 |
Softening Point - DMA | 178 | °F | 内部方法 |
干燥温度 | 230 到 248 | °F |
|
干燥时间 | 2.0 到 3.0 | hr |
|
建议的最大水分含量 | 0.030 | % |
|
料筒后部温度 | 374 到 428 | °F |
|
料筒中部温度 | 374 到 428 | °F |
|
料筒前部温度 | 374 到 428 | °F |
|
射嘴温度 | 410 到 437 | °F |
|
干燥温度 | 230 到 248 | °F |
|
干燥时间 | 2.0 到 3.0 | hr |
|
料筒1区温度 | 338 到 410 | °F |
|
料筒3区温度 | 338 到 410 | °F |
|
料筒5区温度 | 338 到 410 | °F |
|
接头温度 | 392 到 428 | °F |
|
口模温度 | 383 到 419 | °F |
|
如需巴斯夫原厂物性表及相关文件，请联系我们工作人员，谢谢！