Ultradur® B 4300 G3
聚丁烯对苯二甲酸酯
产品说明:
Ultradur B 4300 G3 is an easy flowing injection molding PBT with 15% glass fiber reinforcement for rigid, tough, and dimensionally stable parts.
Applications
Typical applications include timer dials, toggles, knobs, parts for thermostats, oven-door handles, toaster housings and grills.
填料/增强材料 | |
特性 | Good Rigidity、尺寸稳定性良好、良好的流动性、韧性良好 |
用途 | 把手、电气元件、外壳、旋钮 |
机构评级 | |
RoHS 合规性 | |
形式 | |
加工方法 | |
密度 / 比重 |
|
|
|
-- | 1.42 |
| ASTM D792 |
-- | 1.42 | g/cm³ | ISO 1183 |
溶化体积流率（MVR） (250°C/2.16 kg) | 1.34 | in³/10min | ISO 1133 |
收缩率 - 流动 (0.125 in) | 5.0E-3 | in/in |
|
吸水率 |
|
|
|
饱和 | 0.40 | % | ASTM D570 |
饱和, 73°F | 0.40 | % | ISO 62 |
平衡, 50% RH | 0.20 | % | ASTM D570 |
平衡, 73°F, 50% RH | 0.20 | % | ISO 62 |
Viscosity Number (Reduced Viscosity) | 111.0 | ml/g | ISO 1628 |
拉伸模量 (73°F) | 870000 | psi | ISO 527-2 |
抗张强度 (断裂, 73°F) | 13500 | psi | ASTM D638, ISO 527-2 |
伸长率 (断裂, 73°F) | 4.0 | % | ASTM D638, ISO 527-2 |
弯曲模量 |
|
|
|
73°F | 701000 | psi | ASTM D790 |
73°F | 696000 | psi | ISO 178 |
悬壁梁缺口冲击强度 |
|
|
|
-40°F | 0.81 | ft·lb/in | ASTM D256 |
73°F | 0.99 | ft·lb/in | ASTM D256 |
73°F | 2.8 | ft·lb/in² | ISO 180 |
载荷下热变形温度 |
|
|
|
66 psi, 未退火 | 428 | °F | ASTM D648, ISO 75-2/B |
264 psi, 未退火 | 397 | °F | ASTM D648 |
264 psi, 未退火 | 361 | °F | ISO 75-2/A |
熔融峰值温度 | 433 | °F | ASTM D3418, ISO 3146 |
线形热膨胀系数 - 流动 | 2.2E-5 | in/in/°F |
|
RTI Elec |
|
| UL 746 |
0.030 in | 266 | °F |
|
0.06 in | 266 | °F |
|
0.12 in | 266 | °F |
|
RTI Imp |
|
| UL 746 |
0.06 in | 221 | °F |
|
0.12 in | 221 | °F |
|
RTI (0.12 in) | 284 | °F | UL 746 |
表面电阻率 |
|
|
|
0.0591 in | 1.0E+13 | ohms | ASTM D257 |
-- | 1.0E+13 | ohms | IEC 60093 |
体积电阻率 |
|
|
|
0.0591 in | > 1.0E+15 | ohms·cm | ASTM D257 |
-- | > 1.0E+15 | ohms·cm | IEC 60093 |
介电常数 |
|
| IEC 60250 |
100 Hz | 3.70 |
|
|
1 MHz | 3.70 |
|
|
耗散因数 |
|
| IEC 60250 |
100 Hz | 1.2E-3 |
|
|
1 MHz | 0.015 |
|
|
UL 阻燃等级 |
|
| UL 94 |
0.030 in | HB |
|
|
0.06 in | HB |
|
|
0.12 in | HB |
|
|
干燥温度 | 212 到 248 | °F |
|
干燥时间 | 4.0 | hr |
|
建议的最大水分含量 | 0.040 | % |
|
加工（熔体）温度 | 482 到 518 | °F |
|
模具温度 | 140 到 212 | °F |
|
注塑压力 | 508 到 1810 | psi |
|
注射速度 | 快速 |
|
|
背压 | < 145 | psi |
|
如需巴斯夫原厂物性表及相关文件，请联系我们工作人员，谢谢！