Ultramid® B3L
聚酰胺6
产品说明:
Ultramid B3L is an impact-modified, easy flowing injection molding PA6 grade for fast processing.
Applications
Typical applications include impact-resistant articles such as housings, fittings, small parts and anchors.
添加剂 | 冲击改性剂 |
特性 | 冲击改性、抗撞击性，良好、快的成型周期、良好的流动性、耐油性能 |
用途 | 配件外壳 |
机构评级 | EC 1907/2006 (REACH) |
RoHS 合规性 | RoHS 合规 |
形式 | 粒子 |
加工方法 | 注射成型 |
多点数据 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
密度 / 比重 |
|
|
|
|
-- | 1.10 | -- |
| ASTM D792 |
-- | 1.10 | -- | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (275°C/5.0 kg) | 6.10 | -- | in³/10min | ISO 1133 |
收缩率 - 流动 (0.125 in) | 0.011 | -- | in/in |
|
吸水率 |
|
|
|
|
饱和 | 9.0 | -- | % | ASTM D570 |
饱和, 73°F | 9.0 | -- | % | ISO 62 |
平衡, 50% RH | 2.5 | -- | % | ASTM D570 |
平衡, 73°F, 50% RH | 2.5 | -- | % | ISO 62 |
拉伸模量 (73°F) | 406000 | 131000 | psi | ISO 527-2 |
抗张强度 |
|
|
|
|
屈服, 73°F | 10000 | -- | psi | ASTM D638 |
屈服, 73°F | 10200 | 5080 | psi | ISO 527-2 |
伸长率 |
|
|
|
|
屈服, 73°F | 4.0 | -- | % | ASTM D638 |
屈服, 73°F | 4.0 | 18 | % | ISO 527-2 |
断裂, 73°F | 25 | -- | % | ASTM D638 |
标称拉伸断裂应变 (73°F) | 25 | > 50 | % | ISO 527-2 |
弯曲模量 |
|
|
|
|
73°F | 363000 | -- | psi | ASTM D790 |
73°F | 334000 | -- | psi | ISO 178 |
简支梁缺口冲击强度 |
|
|
| ISO 179 |
-22°F | 2.9 | -- | ft·lb/in² |
|
73°F | 4.8 ft·lb/in² | 无断裂 |
|
|
简支梁无缺口冲击强度 |
|
|
| ISO 179 |
-22°F | 无断裂 | -- |
|
|
73°F | 无断裂 | 无断裂 |
|
|
悬壁梁缺口冲击强度 |
|
|
|
|
-40°F | 0.99 | -- | ft·lb/in | ASTM D256 |
73°F | 2.5 | -- | ft·lb/in | ASTM D256 |
73°F | 7.1 | -- | ft·lb/in² | ISO 180 |
载荷下热变形温度 |
|
|
|
|
66 psi, 未退火 | 320 | -- | °F | ASTM D648 |
66 psi, 未退火 | 302 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 151 | -- | °F | ASTM D648 |
264 psi, 未退火 | 149 | -- | °F | ISO 75-2/A |
熔融峰值温度 | 428 | -- | °F | ASTM D3418, ISO 3146 |
线形热膨胀系数 - 流动 |
|
|
|
|
-- | 2.2E-5 | -- | in/in/°F | ASTM E831 |
-- | 4.7E-5 | -- | in/in/°F |
|
RTI Elec |
|
|
| UL 746 |
0.016 in | 149 | -- | °F |
|
0.031 in | 149 | -- | °F |
|
0.06 in | 149 | -- | °F |
|
0.12 in | 149 | -- | °F |
|
RTI Imp |
|
|
| UL 746 |
0.016 in | 149 | -- | °F |
|
0.031 in | 149 | -- | °F |
|
0.06 in | 149 | -- | °F |
|
0.12 in | 149 | -- | °F |
|
RTI |
|
|
| UL 746 |
0.016 in | 149 | -- | °F |
|
0.031 in | 149 | -- | °F |
|
0.06 in | 149 | -- | °F |
|
0.12 in | 149 | -- | °F |
|
体积电阻率 |
|
|
|
|
0.0591 in | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
-- | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
介电常数 |
|
|
| IEC 60250 |
100 Hz | 4.00 | -- |
|
|
1 MHz | 3.50 | 6.40 |
|
|
耗散因数 |
|
|
| IEC 60250 |
100 Hz | 0.010 | -- |
|
|
1 MHz | 0.024 | 0.24 |
|
|
漏电起痕指数 | 600 | 600 | V | IEC 60112 |
UL 阻燃等级 |
|
|
| UL 94 |
0.016 in | HB | -- |
|
|
0.031 in | HB | -- |
|
|
0.06 in | HB | -- |
|
|
0.12 in | HB | -- |
|
|
如需巴斯夫原厂物性表及相关文件，请联系我们工作人员，谢谢！