Ultrason® E KR 4113
聚醚砜
产品说明:
Compound based on PES with 30 % filler. The filler system, a mixture of carbon fibres, graphite and PTFE powder, considerably improves Ultrason tribological properties. In addition, this product has a very small expansion coefficient and low tendency to swell in hot oils.
填料/增强材料 | |
机构评级 | |
RoHS 合规性 | |
形式 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.48 | g/cm³ | ISO 1183 |
表观密度 | 0.70 到 0.80 | g/cm³ |
|
溶化体积流率（MVR） (360°C/10.0 kg) | 0.610 | in³/10min | ISO 1133 |
收缩率 |
|
| ISO 294-4 |
横向流量 | 0.46 | % |
|
流量 | 0.31 | % |
|
吸水率 |
|
| ISO 62 |
饱和, 73°F | 1.5 | % |
|
平衡, 73°F, 50% RH | 0.50 | % |
|
粘数 2 | 56.0 | cm³/g | ISO 307 |
球压硬度 (H 961/30) | 26100 | psi | ISO 2039-1 |
拉伸模量 | 1.60E+6 | psi | ISO 527-2 |
拉伸应力 (断裂) | 16700 | psi | ISO 527-2 |
拉伸应变 (断裂) | 1.5 | % | ISO 527-2 |
简支梁缺口冲击强度 |
|
| ISO 179/1eA |
-22°F | 2.4 | ft·lb/in² |
|
73°F | 3.1 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
| ISO 179/1eU |
-22°F | 9.5 | ft·lb/in² |
|
73°F | 11 | ft·lb/in² |
|
悬壁梁缺口冲击强度 |
|
| ISO 180/A |
-22°F | 2.6 | ft·lb/in² |
|
73°F | 3.1 | ft·lb/in² |
|
热变形温度 (264 psi, 未退火) | 433 | °F | ISO 75-2/A |
玻璃转化温度 3 | 437 | °F | ISO 11357-2 |
线形热膨胀系数 - 流动 |
|
|
|
73 到 176°F | 6.1E-6 | in/in/°F | ISO 11359-2 |
356°F | 7.2E-6 | in/in/°F | DIN 53752 |
表面电阻率 | 4.0E+3 | ohms | IEC 60093 |
体积电阻率 | 9.0E+5 | ohms·cm | IEC 60093 |
介电强度 | 200 | V/mil | IEC 60243-1 |
干燥温度 | 284 | °F |
|
干燥时间 | 4.0 | hr |
|
建议的最大水分含量 | 0.020 | % |
|
料斗温度 | 176 | °F |
|
料筒后部温度 | 662 | °F |
|
料筒中部温度 | 680 | °F |
|
料筒前部温度 | 698 | °F |
|
射嘴温度 | 698 | °F |
|
加工（熔体）温度 | 662 到 734 | °F |
|
模具温度 | 302 到 374 | °F |
|
Screw Speed | < 709 | in/min |
|