Ultramid® A3WG5
聚酰胺66
产品说明:
Ultramid A3WG5 is a 25% glass fiber reinforced and heat resistance injection molding PA66 grade.
Applications
Typical applications include machinery components and housings of high stiffness and dimensional stability such as coil formers and bearing cages. A3EG5 and A3HG5 are the preferred grades for producing electrically insulating parts.
填料/增强材料 | 玻璃纤维增强材料, 25% 填料按重量 |
特性 | Good Heat Resistance、High Dimensional Stability、刚性，高、耐油性能 |
用途 | 机器/机械部件、外壳 |
机构评级 | EC 1907/2006 (REACH) |
RoHS 合规性 | RoHS 合规 |
形式 | 粒子 |
加工方法 | 注射成型 |
多点数据 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
密度 / 比重 |
|
|
|
|
-- | 1.32 | -- |
| ASTM D792 |
-- | 1.32 | -- | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (275°C/5.0 kg) | 3.05 | -- | in³/10min | ISO 1133 |
收缩率 - 流动 (0.125 in) | 3.0E-3 | -- | in/in |
|
吸水率 |
|
|
|
|
饱和 | 6.0 | -- | % | ASTM D570 |
饱和, 73°F | 6.0 | -- | % | ISO 62 |
平衡, 50% RH | 1.9 | -- | % | ASTM D570 |
平衡, 73°F, 50% RH | 1.9 | -- | % | ISO 62 |
拉伸模量 (73°F) | 1.25E+6 | 943000 | psi | ISO 527-2 |
抗张强度 |
|
|
|
|
断裂, 73°F | 24500 | 17100 | psi | ASTM D638 |
断裂, 73°F | 26100 | 17400 | psi | ISO 527-2 |
伸长率 |
|
|
|
|
断裂, 73°F | 2.8 | 5.0 | % | ASTM D638 |
断裂, 73°F | 2.8 | 6.0 | % | ISO 527-2 |
弯曲模量 |
|
|
|
|
73°F | 1.12E+6 | 780000 | psi | ASTM D790 |
73°F | 1.10E+6 | -- | psi | ISO 178 |
简支梁缺口冲击强度 |
|
|
| ISO 179 |
-22°F | 4.3 | -- | ft·lb/in² |
|
73°F | 4.8 | 9.5 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
|
| ISO 179 |
-22°F | 26 | -- | ft·lb/in² |
|
73°F | 29 | 43 | ft·lb/in² |
|
悬壁梁缺口冲击强度 |
|
|
|
|
-40°F | 1.3 | -- | ft·lb/in | ASTM D256 |
73°F | 1.5 | -- | ft·lb/in | ASTM D256 |
73°F | 4.5 | -- | ft·lb/in² | ISO 180 |
载荷下热变形温度 |
|
|
|
|
66 psi, 未退火 | 482 | -- | °F | ASTM D648, ISO 75-2/B |
264 psi, 未退火 | 482 | -- | °F | ASTM D648, ISO 75-2/A |
熔融峰值温度 | 500 | -- | °F | ASTM D3418, ISO 3146 |
线形热膨胀系数 |
|
|
|
|
流动 | 5.6E-6 | -- | in/in/°F | ASTM E831 |
流动 | 1.7E-5 | -- | in/in/°F |
|
横向 | 3.6E-5 | -- | in/in/°F |
|
RTI Elec |
|
|
| UL 746 |
0.028 in | 257 | -- | °F |
|
0.06 in | 257 | -- | °F |
|
0.12 in | 257 | -- | °F |
|
RTI Imp |
|
|
| UL 746 |
0.06 in | 248 | -- | °F |
|
0.12 in | 257 | -- | °F |
|
RTI |
|
|
| UL 746 |
0.06 in | 239 | -- | °F |
|
0.12 in | 266 | -- | °F |
|
体积电阻率 |
|
|
|
|
0.0591 in | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
-- | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
介电常数 (1 MHz) | 3.50 | 5.50 |
| IEC 60250 |
耗散因数 |
|
|
| IEC 60250 |
100 Hz | 0.014 | 0.30 |
|
|
1 MHz | 0.014 | 0.30 |
|
|
漏电起痕指数 | 450 | 450 | V | IEC 60112 |
UL 阻燃等级 |
|
|
| UL 94 |
0.028 in | HB | -- |
|
|
0.06 in | HB | -- |
|
|
0.12 in | HB | -- |
|
|
干燥温度 | 176 | °F |
|
干燥时间 | 2.0 到 4.0 | hr |
|
建议的最大水分含量 | 0.15 | % |
|
加工（熔体）温度 | 536 到 581 | °F |
|
模具温度 | 176 到 194 | °F |
|
注塑压力 | 508 到 1810 | psi |
|
注射速度 | 快速 |
|
|