Ultramid® A3HG5
聚酰胺66
产品说明:
Ultramid A3HG5 is a 25% glass fiber reinforced injection molding PA66 grade.
Applications
Typical applications include machinery components and housings of high stiffness and dimensional stability.
填料/增强材料 | 玻璃纤维增强材料, 25% 填料按重量 |
特性 | High Dimensional Stability、刚性，高、耐油性能 |
用途 | 机器/机械部件外壳 |
机构评级 | EC 1907/2006 (REACH) |
RoHS 合规性 | RoHS 合规 |
形式 | 粒子 |
加工方法 | 注射成型 |
多点数据 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
密度 / 比重 |
|
|
|
|
-- | 1.32 | -- |
| ASTM D792 |
-- | 1.32 | -- | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (275°C/5.0 kg) | 3.05 | -- | in³/10min | ISO 1133 |
收缩率 - 流动 (0.125 in) | 3.0E-3 | -- | in/in |
|
吸水率 |
|
|
|
|
饱和 | 6.0 | -- | % | ASTM D570 |
饱和, 73°F | 6.0 | -- | % | ISO 62 |
平衡, 50% RH | 1.9 | -- | % | ASTM D570 |
平衡, 73°F, 50% RH | 1.9 | -- | % | ISO 62 |
拉伸模量 (73°F) | 1.25E+6 | 943000 | psi | ISO 527-2 |
抗张强度 |
|
|
|
|
断裂, 73°F | 26000 | -- | psi | ASTM D638 |
断裂, -40°F | 28400 | 27000 | psi | ISO 527-2 |
断裂, 73°F | 24700 | 17400 | psi | ISO 527-2 |
伸长率 |
|
|
|
|
断裂, 73°F | 3.0 | -- | % | ASTM D638 |
断裂, -40°F | 2.9 | 2.7 | % | ISO 527-2 |
断裂, 73°F | 3.0 | 6.0 | % | ISO 527-2 |
弯曲模量 |
|
|
|
|
73°F | 1.15E+6 | -- | psi | ASTM D790 |
73°F | 1.10E+6 | -- | psi | ISO 178 |
简支梁缺口冲击强度 |
|
|
| ISO 179 |
-22°F | 4.3 | -- | ft·lb/in² |
|
73°F | 4.8 | 8.6 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
|
| ISO 179 |
-22°F | 26 | -- | ft·lb/in² |
|
73°F | 31 | 43 | ft·lb/in² |
|
悬壁梁缺口冲击强度 |
|
|
|
|
-40°F | 0.99 | -- | ft·lb/in | ASTM D256 |
73°F | 1.8 | -- | ft·lb/in | ASTM D256 |
73°F | 4.5 | -- | ft·lb/in² | ISO 180 |
载荷下热变形温度 |
|
|
|
|
66 psi, 未退火 | 482 | -- | °F | ASTM D648, ISO 75-2/B |
264 psi, 未退火 | 482 | -- | °F | ASTM D648, ISO 75-2/A |
熔融峰值温度 | 500 | -- | °F | ASTM D3418, ISO 3146 |
线形热膨胀系数 |
|
|
|
|
流动 | 5.6E-6 | -- | in/in/°F | ASTM E831 |
流动 | 1.7E-5 | -- | in/in/°F |
|
横向 | 3.6E-5 | -- | in/in/°F |
|
RTI Elec |
|
|
| UL 746 |
0.031 in | 266 | -- | °F |
|
0.06 in | 266 | -- | °F |
|
0.12 in | 266 | -- | °F |
|
RTI Imp |
|
|
| UL 746 |
0.06 in | 248 | -- | °F |
|
0.12 in | 248 | -- | °F |
|
RTI |
|
|
| UL 746 |
0.06 in | 266 | -- | °F |
|
0.12 in | 266 | -- | °F |
|
体积电阻率 |
|
|
|
|
0.0591 in | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
-- | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
介电常数 (1 MHz) | 3.50 | 5.50 |
| IEC 60250 |
耗散因数 |
|
|
| IEC 60250 |
100 Hz | 0.014 | 0.30 |
|
|
1 MHz | 0.014 | 0.16 |
|
|
漏电起痕指数 | 550 | 550 | V | IEC 60112 |
UL 阻燃等级 |
|
|
| UL 94 |
0.031 in | HB | -- |
|
|
0.06 in | HB | -- |
|
|
0.12 in | HB | -- |
|
|
干燥温度 | 176 | °F |
|
干燥时间 | 2.0 到 4.0 | hr |
|
建议的最大水分含量 | 0.15 | % |
|
加工（熔体）温度 | 536 到 581 | °F |
|
模具温度 | 176 到 194 | °F |
|
注塑压力 | 508 到 1810 | psi |
|
注射速度 | 快速 |
|
|
如需巴斯夫原厂物性表及相关文件，请联系我们工作人员，谢谢！