Ultramid® A3HG2
聚酰胺66
产品说明:
Ultramid A3HG2 is a 10% glass fiber reinforced injection molding PA66 grade.
Applications
Typical applications include machinery components and housings of medium stiffness, as well as electrically insulating parts.
填料/增强材料 | 玻璃纤维增强材料, 10% 填料按重量 |
特性 | Medium Stiffness、绝缘、耐油性能 |
用途 | 电气元件、机器/机械部件、外壳 |
机构评级 | EC 1907/2006 (REACH) |
RoHS 合规性 | RoHS 合规 |
形式 | 粒子 |
加工方法 | 注射成型 |
密度 / 比重 |
|
|
|
|
-- | 1.20 | -- |
| ASTM D792 |
-- | 1.20 | -- | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (275°C/5.0 kg) | 4.88 | -- | in³/10min | ISO 1133 |
收缩率 - 流动 (0.125 in) | 8.0E-3 | -- | in/in |
|
吸水率 |
|
|
|
|
饱和 | 7.0 | -- | % | ASTM D570 |
饱和, 73°F | 7.0 | -- | % | ISO 62 |
平衡, 50% RH | 2.1 | -- | % | ASTM D570 |
平衡, 73°F, 50% RH | 2.1 | -- | % | ISO 62 |
拉伸模量 (73°F) | 667000 | 377000 | psi | ISO 527-2 |
抗张强度 |
|
|
|
|
断裂, 73°F | 14500 | -- | psi | ASTM D638 |
断裂, 73°F | 14500 | 8700 | psi | ISO 527-2 |
伸长率 |
|
|
|
|
断裂, 73°F | 3.0 | -- | % | ASTM D638 |
断裂, 73°F | 3.0 | 12 | % | ISO 527-2 |
弯曲模量 (73°F) | 650000 | -- | psi | ASTM D790, ISO 178 |
简支梁缺口冲击强度 (73°F) | 3.3 | 4.3 | ft·lb/in² | ISO 179 |
简支梁无缺口冲击强度 (73°F) | 14 | 44 | ft·lb/in² | ISO 179 |
悬壁梁缺口冲击强度 |
|
|
|
|
73°F | 0.99 | -- | ft·lb/in | ASTM D256 |
73°F | 2.6 | -- | ft·lb/in² | ISO 180 |
载荷下热变形温度 (264 psi, 未退火) | 410 | -- | °F | ASTM D648, ISO 75-2/A |
熔融峰值温度 | 500 | -- | °F | ASTM D3418, ISO 3146 |
线形热膨胀系数 |
|
|
|
|
流动 | 1.8E-5 | -- | in/in/°F |
|
横向 | 4.2E-5 | -- | in/in/°F |
|
体积电阻率 |
|
|
|
|
0.0591 in | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
-- | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
介电常数 (1 MHz) | 3.50 | 5.50 |
| IEC 60250 |
耗散因数 (1 MHz) | 0.014 | 0.16 |
| IEC 60250 |
漏电起痕指数 | 550 | 550 | V | IEC 60112 |
干燥温度 | 176 | °F |
|
干燥时间 | 2.0 到 4.0 | hr |
|
建议的最大水分含量 | 0.15 | % |
|
加工（熔体）温度 | 536 到 581 | °F |
|
模具温度 | 176 到 194 | °F |
|
注塑压力 | 508 到 1810 | psi |
|
注射速度 | 快速 |
|
|