Ultramid® A3EG3
聚酰胺66
产品说明:
Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade.
Applications
Typical applications include medium stiffness machinery components and housings, as well as electrically insulating parts.
填料/增强材料 | 玻璃纤维增强材料, 15% 填料按重量 |
特性 | 刚性，良好、耐油性能 |
用途 | 电气元件、电子绝缘、机器/机械部件、外壳 |
机构评级 | EC 1907/2006 (REACH) |
RoHS 合规性 | RoHS 合规 |
形式 | 粒子 |
加工方法 | 注射成型 |
多点数据 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
密度 / 比重 |
|
|
|
|
-- | 1.24 | -- |
| ASTM D792 |
-- | 1.24 | -- | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (275°C/5.0 kg) | 4.27 | -- | in³/10min | ISO 1133 |
收缩率 - 流动 (0.125 in) | 5.5E-3 | -- | in/in |
|
吸水率 |
|
|
|
|
饱和 | 7.0 | -- | % | ASTM D570 |
饱和, 73°F | 7.0 | -- | % | ISO 62 |
平衡, 50% RH | 2.2 | -- | % | ASTM D570 |
平衡, 73°F, 50% RH | 2.2 | -- | % | ISO 62 |
拉伸模量 (73°F) | 870000 | 653000 | psi | ISO 527-2 |
抗张强度 |
|
|
|
|
断裂, 73°F | 16500 | -- | psi | ASTM D638 |
断裂, -40°F | 22600 | -- | psi | ISO 527-2 |
断裂, 73°F | 18900 | 12300 | psi | ISO 527-2 |
伸长率 |
|
|
|
|
断裂, 73°F | 3.0 | -- | % | ASTM D638 |
断裂, -40°F | 2.6 | -- | % | ISO 527-2 |
断裂, 73°F | 3.0 | 10 | % | ISO 527-2 |
弯曲模量 |
|
|
|
|
73°F | 750000 | -- | psi | ASTM D790 |
73°F | 754000 | 580000 | psi | ISO 178 |
弯曲应力 (73°F) | 26100 | 18100 | psi | ISO 178 |
简支梁缺口冲击强度 |
|
|
| ISO 179 |
-22°F | 3.3 | -- | ft·lb/in² |
|
73°F | 3.8 | 5.2 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
|
| ISO 179 |
-22°F | 20 | -- | ft·lb/in² |
|
73°F | 21 | 33 | ft·lb/in² |
|
悬壁梁缺口冲击强度 |
|
|
|
|
-40°F | 0.99 | -- | ft·lb/in | ASTM D256 |
73°F | 1.1 | -- | ft·lb/in | ASTM D256 |
73°F | 2.6 | 6.7 | ft·lb/in² | ISO 180 |
载荷下热变形温度 |
|
|
|
|
66 psi, 未退火 | 482 | -- | °F | ASTM D648, ISO 75-2/B |
264 psi, 未退火 | 482 | -- | °F | ASTM D648, ISO 75-2/A |
熔融峰值温度 | 500 | -- | °F | ASTM D3418, ISO 3146 |
线形热膨胀系数 |
|
|
|
|
流动 | 1.1E-5 | -- | in/in/°F | ASTM E831 |
流动 | 1.8E-5 | -- | in/in/°F |
|
横向 | 4.2E-5 | -- | in/in/°F |
|
RTI Elec |
|
|
| UL 746 |
0.031 in | 266 | -- | °F |
|
0.06 in | 266 | -- | °F |
|
0.12 in | 266 | -- | °F |
|
RTI Imp |
|
|
| UL 746 |
0.06 in | 257 | -- | °F |
|
0.12 in | 257 | -- | °F |
|
RTI |
|
|
| UL 746 |
0.06 in | 257 | -- | °F |
|
0.12 in | 257 | -- | °F |
|
体积电阻率 |
|
|
|
|
0.0591 in | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
-- | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
介电常数 (1 MHz) | 3.50 | 5.50 |
| IEC 60250 |
耗散因数 |
|
|
| IEC 60250 |
100 Hz | 0.014 | 0.30 |
|
|
1 MHz | 0.023 | 0.16 |
|
|
漏电起痕指数 | 550 | 550 | V | IEC 60112 |
UL 阻燃等级 |
|
|
| UL 94 |
0.031 in | HB | -- |
|
|
0.06 in | HB | -- |
|
|
0.12 in | HB | -- |
|
|
如需巴斯夫原厂物性表及相关文件，请联系我们工作人员，谢谢！