Akulon® Ultraflow K-FHG6/B
聚酰胺6
产品说明:
30% Glass Reinforced, Heat Stabilized, High Flow, Improved Processing
Special Features:
Used In:
Akulon® is our family of high performance polyamide 6 and polyamide 66 materials, used by customers across the world in applications ranging from automotive, electronics & electrical, to furniture and packaging.
We offer Akulon® grades for injection molding, blow molding and extrusion (including barrier film, stock shapes, convoluted tubes, and mono and multi filament).
In molded parts the material offers an excellent balance of easy design and processing with outstanding mechanical properties over a wide temperature range and in diverse conditions. Meanwhile for extrusion the strength, resilience and easy processing of Akulon® sets the market standards.
填料/增强材料 | |
添加剂 | |
特性 | |
用途 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.35 | -- | g/cm³ | ISO 1183 |
收缩率 |
|
|
| ISO 294-4 |
横向流量 | 1.1 | -- | % |
|
流量 | 0.30 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
饱和, 73°F | 6.0 | -- | % |
|
平衡, 73°F, 50% RH | 1.8 | -- | % |
|
拉伸模量 | 1.36E+6 | 827000 | psi | ISO 527-2 |
拉伸应力 (断裂) | 23200 | 15200 | psi | ISO 527-2 |
拉伸应变 (断裂) | 3.0 | 7.0 | % | ISO 527-2 |
弯曲模量 | 1.23E+6 | -- | psi | ISO 178 |
弯曲应力 | 34100 | -- | psi | ISO 178 |
简支梁缺口冲击强度 |
|
|
| ISO 179/1eA |
-22°F | 4.8 | 4.8 | ft·lb/in² |
|
73°F | 6.7 | 10 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
|
| ISO 179/1eU |
-22°F | 31 | 31 | ft·lb/in² |
|
73°F | 40 | 43 | ft·lb/in² |
|
热变形温度 |
|
|
|
|
66 psi, 未退火 | 428 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 392 | -- | °F | ISO 75-2/A |
熔融温度 2 | 428 | -- | °F | ISO 11357-3 |
线形热膨胀系数 |
|
|
| ISO 11359-2 |
流动 | 1.1E-5 | -- | in/in/°F |
|
横向 | 3.9E-5 | -- | in/in/°F |
|
Effective Thermal Diffusivity | 1.08E-7 | -- | m²/s |
|
体积电阻率 | > 1.0E+15 | 1.0E+14 | ohms·cm | IEC 60093 |
相对电容率 |
|
|
| IEC 60250 |
100 Hz | 3.50 | 14.0 |
|
|
1 MHz | 3.30 | 5.00 |
|
|
耗散因数 |
|
|
| IEC 60250 |
100 Hz | 5.0E-3 | 0.30 |
|
|
1 MHz | 0.015 | 0.12 |
|
|
漏电起痕指数 | -- | 500 | V | IEC 60112 |
可燃性等级 (0.06 in) | HB | -- |
| IEC 60695-11-10, -20 |
熔体密度 | 1.12 | -- | g/cm³ |
|
熔体导热性 | 1.9 | -- | Btu·in/hr/ft²/°F |
|
Specific Heat Capacity of Melt | 0.538 | -- | Btu/lb/°F |
|
干燥温度 | 176 | °F |
干燥时间 | 4.0 到 8.0 | hr |
料筒后部温度 | 446 到 482 | °F |
料筒中部温度 | 446 到 500 | °F |
料筒前部温度 | 446 到 500 | °F |
射嘴温度 | 482 到 536 | °F |
加工（熔体）温度 | 473 到 518 | °F |
模具温度 | 104 到 176 | °F |
注射速度 | 中等偏快 |
|
背压 | 435 到 1450 | psi |
螺杆压缩比 | 2.5:1.0 |
|
如需帝斯曼原厂物性表及相关文件，请联系我们工作人员，谢谢！