Arnite® TV4 220
聚丁烯对苯二甲酸酯
产品说明:
10% Glass Reinforced
Special Features:
Used In:
Arnite® (PBT, PET and blends) are high-performance engineering plastics that combine high strength and rigidity with excellent processing characteristics. As a result, Arnite® A (PET) and Arnite® T (PBT) are well suited for a broad range of automotive, electrical & electronic and consumer goods applications.
A wide portfolio of Arnite® is available including unreinforced, reinforced and flame retardant grades.
填料/增强材料 | |
添加剂 | |
加工方法 | |
多点数据 | Specific Heat vs. Temperature (ISO 11403-2)
|
树脂ID (ISO 1043) | |
密度 | 1.37 | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (250°C/2.16 kg) | 1.28 | in³/10min | ISO 1133 |
收缩率 |
|
| ISO 294-4 |
横向流量 | 1.5 | % |
|
流量 | 0.85 | % |
|
吸水率 |
|
| ISO 62 |
饱和, 73°F | 0.35 | % |
|
平衡, 73°F, 50% RH | 0.16 | % |
|
拉伸模量 | 667000 | psi | ISO 527-2 |
拉伸应力 (断裂) | 13100 | psi | ISO 527-2 |
拉伸应变 (断裂) | 4.0 | % | ISO 527-2 |
简支梁缺口冲击强度 |
|
| ISO 179/1eA |
-22°F | 2.4 | ft·lb/in² |
|
73°F | 1.9 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
| ISO 179/1eU |
-22°F | 14 | ft·lb/in² |
|
73°F | 16 | ft·lb/in² |
|
熔融温度 2 | 437 | °F | ISO 11357-3 |
线形热膨胀系数 |
|
| ISO 11359-2 |
流动 | 3.3E-5 | in/in/°F |
|
横向 | 4.4E-5 | in/in/°F |
|
体积电阻率 | > 1.0E+15 | ohms·cm | IEC 60093 |
可燃性等级 (0.06 in) | HB |
| IEC 60695-11-10, -20 |
干燥温度 | 212 到 248 | °F |
|
干燥时间 | 3.0 到 12 | hr |
|
料筒后部温度 | 446 到 464 | °F |
|
料筒中部温度 | 446 到 482 | °F |
|
料筒前部温度 | 464 到 500 | °F |
|
射嘴温度 | 464 到 500 | °F |
|
加工（熔体）温度 | 464 到 518 | °F |
|
模具温度 | 140 到 212 | °F |
|
注射速度 | 中等偏快 |
|
|
背压 | 435 到 1450 | psi |
|
螺杆压缩比 | 2.5:1.0 |
|
|