Arnite® B604T
聚丁烯对苯二甲酸酯
产品说明:
Arnite® (PBT, PET and blends) are high-performance engineering plastics that combine high strength and rigidity with excellent processing characteristics. As a result, Arnite® A (PET) and Arnite® T (PBT) are well suited for a broad range of automotive, electrical & electronic and consumer goods applications.
A wide portfolio of Arnite® is available including unreinforced, reinforced and flame retardant grades.
添加剂 | |
特性 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.22 | g/cm³ | ISO 1183 |
吸水率 |
|
| ISO 62 |
饱和, 73°F | 0.40 | % |
|
平衡, 73°F, 50% RH | 0.15 | % |
|
拉伸模量 | 290000 | psi | ISO 527-2 |
拉伸应力 (屈服) | 6380 | psi | ISO 527-2 |
拉伸应变 (屈服) | 3.2 | % | ISO 527-2 |
标称拉伸断裂应变 | 15 | % | ISO 527-2 |
简支梁缺口冲击强度 (73°F) | 无断裂 |
| ISO 179/1eA |
简支梁无缺口冲击强度 (73°F) | 2.6 | ft·lb/in² | ISO 179/1eU |
热变形温度 |
|
|
|
66 psi, 未退火 | 257 | °F | ISO 75-2/B |
264 psi, 未退火 | 122 | °F | ISO 75-2/A |
线形热膨胀系数 |
|
| ISO 11359-2 |
流动 | 5.3E-5 | in/in/°F |
|
横向 | 5.3E-5 | in/in/°F |
|
干燥温度 | 212 到 248 | °F |
|
干燥时间 | 3.0 到 12 | hr |
|
料筒后部温度 | 446 到 464 | °F |
|
料筒中部温度 | 446 到 482 | °F |
|
料筒前部温度 | 464 到 500 | °F |
|
射嘴温度 | 464 到 500 | °F |
|
加工（熔体）温度 | 464 到 518 | °F |
|
模具温度 | 140 到 212 | °F |
|
注射速度 | 中等偏快 |
|
|
背压 | 435 到 1450 | psi |
|
螺杆压缩比 | 2.5:1.0 |
|
|
如需帝斯曼原厂物性表及相关文件，请联系我们工作人员，谢谢！