ForTii® F11C
Polyamide 4T
产品说明:
30% Glass Reinforced, Flame Retardant, Halogen free and free of red phosphorous, Improved color stability
Special Features:
Used In:
ForTii® is a breakthrough high temperature polyamide with halogen-free flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries.
We developed ForTii® in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want €" and need.
That means a high temperature polyamide with a broad and versatile portfolio of grades that deliver high performance with a unique balance of properties.
填料/增强材料 | |
添加剂 | |
特性 | |
用途 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.46 | -- | g/cm³ | ISO 1183 |
收缩率 |
|
|
| ISO 294-4 |
横向流量 | 1.2 | -- | % |
|
流量 | 0.30 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
饱和, 73°F | 4.6 | -- | % |
|
平衡, 73°F, 50% RH | 1.6 | -- | % |
|
粘数 | 86.0 | -- | cm³/g | ISO 307 |
拉伸模量 |
|
|
| ISO 527-2 |
-- | 1.74E+6 | 1.74E+6 | psi |
|
248°F | 1.16E+6 | -- | psi |
|
320°F | 798000 | -- | psi |
|
拉伸应力 |
|
|
| ISO 527-2 |
断裂 | 22500 | 22500 | psi |
|
断裂, 248°F | 15200 | -- | psi |
|
断裂, 320°F | 10900 | -- | psi |
|
拉伸应变 |
|
|
| ISO 527-2 |
断裂 | 2.0 | 2.0 | % |
|
断裂, 248°F | 2.7 | -- | % |
|
断裂, 320°F | 3.7 | -- | % |
|
弯曲模量 | 1.67E+6 | 1.67E+6 | psi | ISO 178 |
弯曲应力 | 35500 | 33400 | psi | ISO 178 |
简支梁缺口冲击强度 (73°F) | 4.8 | 4.8 | ft·lb/in² | ISO 179/1eA |
简支梁无缺口冲击强度 (73°F) | 24 | 24 | ft·lb/in² | ISO 179/1eU |
热变形温度 |
|
|
|
|
66 psi, 未退火 | 613 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 581 | -- | °F | ISO 75-2/A |
玻璃转化温度 3 | 257 | -- | °F | ISO 11357-2 |
熔融温度 3 | 617 | -- | °F | ISO 11357-3 |
线形热膨胀系数 |
|
|
| ASTM D696 |
流动 | 1.7E-5 | -- | in/in/°F |
|
横向 | 1.9E-5 | -- | in/in/°F |
|
RTI Elec (0.0079 in) | 239 | -- | °F | UL 746 |
介电强度 | 840 | 840 | V/mil | IEC 60243-1 |
相对电容率 |
|
|
| IEC 60250 |
100 Hz | 4.20 | 4.20 |
|
|
1 MHz | 3.90 | 3.90 |
|
|
1.00 GHz | 3.90 | 3.90 |
|
|
10.0 GHz | 3.90 | 3.80 |
|
|
耗散因数 |
|
|
| IEC 60250 |
100 Hz | 6.4E-3 | 6.4E-3 |
|
|
1 MHz | 0.018 | 0.018 |
|
|
漏电起痕指数 | 600 | -- | V | IEC 60112 |
可燃性等级 |
|
|
| IEC 60695-11-10, -20 |
0.0079 in | V-0 | -- |
|
|
0.06 in | V-0 | -- |
|
|
极限氧指数 | 39 | -- | % | ISO 4589-2 |
干燥温度 | 212 | °F |
|
干燥时间 | 4.0 到 8.0 | hr |
|
料筒后部温度 | 608 到 626 | °F |
|
料筒中部温度 | 617 到 635 | °F |
|
料筒前部温度 | 626 到 635 | °F |
|
射嘴温度 | 626 到 635 | °F |
|
加工（熔体）温度 | 626 到 644 | °F |
|
模具温度 | 212 到 302 | °F |
|
注射速度 | 中等偏快 |
|
|
背压 | 72.5 到 435 | psi |
|
螺杆压缩比 | 2.5:1.0 |
|
|
如需恩骅力（Envalior）原厂物性表及相关文件，请联系我司工作人员，谢谢！