产品中心

ForTii® Eco LDS62

ForTii® Eco LDS62

产品产商:帝斯曼(DSM)
产品产地:欧洲/中国
产品类别:聚酰胺
产品型号:ForTii Eco LDS62
产品规格:25KG/
产品特性:添加脱模剂

ForTii® Eco LDS62

聚酰胺
产品说明:
Glass Reinforced, Laser Direct Structuring (LDS)

Special Features:
  • Contains release agent

  • Laser Direct Structuring


Used In:
  • Antenna Components


ForTii® is a breakthrough high temperature polyamide with halogen-free flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries.
We developed ForTii® in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want €" and need.
That means a high temperature polyamide with a broad and versatile portfolio of grades that deliver high performance with a unique balance of properties.

填料/增强材料
  • 玻璃纤维增强材料

添加剂
  • 脱模

加工方法
  • 注射成型

树脂ID (ISO 1043)
  • PA*-GF

物理性能
干燥
调节后的
单位制
测试方法
密度
1.50
--
g/cm³
ISO 1183
收缩率



ISO 294-4
横向流量
1.2
--
%

流量
0.30
--
%

机械性能
干燥
调节后的
单位制
测试方法
拉伸模量
1.38E+6
--
psi
ISO 527-2
拉伸应力 (断裂)
15200
--
psi
ISO 527-2
拉伸应变 (断裂)
2.3
--
%
ISO 527-2
弯曲模量
1.31E+6
--
psi
ISO 178
弯曲应力
24700
--
psi
ISO 178
冲击性能
干燥
调节后的
单位制
测试方法
简支梁缺口冲击强度 (73°F)
2.1
--
ft·lb/in²
ISO 179/1eA
热性能
干燥
调节后的
单位制
测试方法
热变形温度




66 psi, 未退火
469
--
°F
ISO 75-2/B
264 psi, 未退火
415
--
°F
ISO 75-2/A
熔融温度 2
581
--
°F
ISO 11357-3
线形热膨胀系数



ISO 11359-2
流动
1.1E-5
--
in/in/°F

横向
5.0E-5
--
in/in/°F

RTI Elec (0.016 in)
149
--
°F
UL 746
电气性能
干燥
调节后的

测试方法
相对电容率 (1.00 GHz)
3.60
3.70

IEC 60250
可燃性
干燥
调节后的

测试方法
可燃性等级 (0.016 in)
HB
--

IEC 60695-11-10, -20
注射
干燥
单位制

干燥温度
212
°F

干燥时间
2.0
hr

料筒后部温度
572 到 608
°F

料筒中部温度
581 到 617
°F

料筒前部温度
590 到 617
°F

射嘴温度
590 到 617
°F

加工(熔体)温度
590 到 626
°F

模具温度
176 到 248
°F

注射速度
中等偏快


背压
72.5 到 435
psi

螺杆压缩比
2.5:1.0



如需帝斯曼原厂物性表及相关文件,请联系我们工作人员,谢谢!

产品被广泛应用于塑料改性、汽车、建筑、电子电气、工业、日用品等多种领域

立即咨询
展开