Makroblend® M525
聚碳酸酯+PBT
(PC+PBT) Blend, impact modified, easy release, injection molding grade. Makroblend M525 offers an exceptional low-temperature impact strength, good flowability and excellent chemical resistance. Manufactured according to GMP, tested only according to ISO 10993-5 and ISO 10993-10 for contact with uncompromised skin only; for questions regarding biocompatibility we ask for an email inquiry under plastics@covestro.com.
密度 (73°F) | 1.22 | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (260°C/5.0 kg) | 1.28 | in³/10min | ISO 1133 |
收缩率 |
|
| ISO 2577 |
横向流量 3 | 0.70 到 0.90 | % |
|
横向流量 : 194°F, 1小时 | 0.10 到 0.20 | % |
|
流量 3 | 0.70 到 0.90 | % |
|
流量 : 194°F, 1小时 | 0.10 到 0.20 | % |
|
拉伸模量 (73°F) | 290000 | psi | ISO 527-2/1 |
拉伸应力 |
|
| ISO 527-2/50 |
屈服, 73°F | 7980 | psi |
|
断裂, 73°F | 6530 | psi |
|
拉伸应变 (屈服, 73°F) | 4.5 | % | ISO 527-2/50 |
标称拉伸断裂应变 (73°F) | > 50 | % | ISO 527-2/50 |
弯曲模量 4 (73°F) | 290000 | psi | ISO 178 |
弯曲应力 4 (3.5% 应变, 73°F) | 9430 | psi | ISO 178 |
悬壁梁缺口冲击强度 |
|
| ISO 180/A |
-4°F | 21 | ft·lb/in² |
|
73°F | 29 | ft·lb/in² |
|
热变形温度 |
|
|
|
66 psi, 未退火 | 212 | °F | ISO 75-2/B |
264 psi, 未退火 | 167 | °F | ISO 75-2/A |
维卡软化温度 | 252 | °F | ISO 306/B120 |
线形热膨胀系数 |
|
| ISO 11359-2 |
流动 : 73 到 131°F | 5.0E-5 | in/in/°F |
|
横向 : 73 到 131°F | 5.0E-5 | in/in/°F |
|
表面电阻率 | > 1.0E+15 | ohms | IEC 60093 |
体积电阻率 (73°F) | > 1.0E+16 | ohms·cm | IEC 60093 |
漏电起痕指数 |
|
| IEC 60112 |
解决方案 A | 225 | V |
|
解决方案 B | 100 | V |
|