Texin® RxS285
热塑性聚氨酯弹性体（聚酯）
Texin RxS285 resin is an aromatic polyester-based thermoplastic polyurethane. It can be processed by injection molding, extrusion or blow molding.
特性 | - 辐射消毒、环氧乙烷消毒、抗撞击性良好、良好的柔韧性、良好耐磨损性、热消毒、韧性良好
|
用途 | |
机构评级 | |
加工方法 | |
密度 / 比重 |
|
|
|
-- | 1.20 |
| ASTM D792 |
-- | 1.20 | g/cm³ | ISO 1183 |
熔流率（熔体流动速率） (190°C/8.7 kg) | 4.0 | g/10 min | ASTM D1238, ISO 1133 |
收缩率 |
|
|
|
流动 : 0.100 in | 8.0E-3 | in/in | ASTM D955 |
横向流动 : 0.100 in | 8.0E-3 | in/in | ASTM D955 |
横向流量 : 0.100 in | 0.80 | % | ISO 2577 |
流量 : 0.100 in | 0.80 | % | ISO 2577 |
肖氏硬度 (邵氏 A) | 85 |
| ASTM D2240, ISO 868 |
弯曲模量 (73°F) | 4000 | psi | ASTM D790, ISO 178 |
泰伯耐磨性 |
|
|
|
1000 Cycles, 1000 g, H-18 转轮 | 35.0 | mg | ASTM D1044 |
1000 Cycles, 1000 g, H-18 转轮 | 35.0 | mg | ISO 4649 |
拉伸应力 |
|
| ASTM D412, ISO 37 |
100%应变 | 775 | psi |
|
300%应变 | 1900 | psi |
|
抗张强度 (屈服) | 5500 | psi | ASTM D412, ISO 37 |
伸长率 (断裂) | 500 | % | ASTM D412, ISO 37 |
撕裂强度 |
|
|
|
-- 2 | 500 | lbf/in | ASTM D624 |
-- | 500 | lbf/in | ISO 34-1 |
压缩永久变形 3 |
|
| ASTM D395B, ISO 815 |
73°F, 22 hr | 12 | % |
|
158°F, 22 hr | 35 | % |
|
维卡软化温度 | 196 | °F | ISO 306/50, ASTM D1525 4 |
黄度指数 |
|
|
|
-- | < 15 | YI | ASTM E313 |
-- | < 15 | YI | DIN 6167 |
干燥温度 - 热风干燥机 | 180 到 210 | °F |
|
干燥时间 - 热风干燥机 | 2.0 | hr |
|
建议的最大水分含量 | < 0.030 | % |
|
料筒后部温度 | 360 到 390 | °F |
|
料筒中部温度 | 360 到 399 | °F |
|
料筒前部温度 | 360 到 410 | °F |
|
射嘴温度 | 370 到 415 | °F |
|
加工（熔体）温度 | 385 到 405 | °F |
|
模具温度 | 61 到 109 | °F |
|
注塑压力 | 6000 到 15000 | psi |
|
注射速度 | 慢到中等 |
|
|
背压 | < 800 | psi |
|
螺杆转速 | 40 到 80 | rpm |
|
垫层 | < 0.125 | in |
|
Hold Pressure: 60 to 80% of Injection Pressure |
干燥温度 | 180 到 210 | °F |
|
干燥时间 | 2.0 | hr |
|
料筒1区温度 | 360 到 390 | °F |
|
料筒2区温度 | 360 到 399 | °F |
|
料筒3区温度 | 360 到 410 | °F |
|
熔体温度 | 707 到 752 | °F |
|
口模温度 | 370 到 410 | °F |
|
如需科思创原厂物性表及相关文件，请联系我们工作人员，谢谢！