Texin® 250
热塑性聚氨酯弹性体（聚酯）
Texin 250 resin is an aromatic polyester-based thermoplastic polyurethane with a Shore hardness of approximately 50D. It is processed primarily by extrusion and blow molding but can also be used for injection molding.
特性 | - 低速凝固晶点、抗溶剂性、良好耐磨损性、耐化学性良好、耐油性能、中等透明度
|
用途 | |
机构评级 | - FDA 21 CFR 177.1680FDA 21 CFR 177.2600
|
外观 | |
加工方法 | |
密度 / 比重 |
|
|
|
-- | 1.22 |
| ASTM D792 |
-- | 1.22 | g/cm³ | ISO 1183 |
收缩率 |
|
|
|
流动 : 0.100 in | 8.0E-3 | in/in | ASTM D955 |
横向流动 : 0.100 in | 8.0E-3 | in/in | ASTM D955 |
横向流量 : 0.100 in | 0.80 | % | ISO 2577 |
流量 : 0.100 in | 0.80 | % | ISO 2577 |
肖氏硬度 |
|
| ASTM D2240, ISO 868 |
邵氏 A | 95 |
|
|
邵氏 D | 50 |
|
|
弯曲模量 |
|
| ASTM D790, ISO 178 |
73°F | 12000 | psi |
|
158°F | 5220 | psi |
|
泰伯耐磨性 |
|
|
|
1000 Cycles, 1000 g, H-18 转轮 | 70.0 | mg | ASTM D1044 |
1000 Cycles, 1000 g, H-18 转轮 | 70.0 | mg | ISO 4649 |
拉伸应力 |
|
| ASTM D412, ISO 37 |
100%应变 | 1700 | psi |
|
300%应变 | 4600 | psi |
|
抗张强度 (屈服) | 6700 | psi | ASTM D412, ISO 37 |
伸长率 (断裂) | 400 | % | ASTM D412, ISO 37 |
撕裂强度 |
|
|
|
-- 2 | 775 | lbf/in | ASTM D624 |
-- | 780 | lbf/in | ISO 34-1 |
压缩永久变形 3 |
|
| ASTM D395B, ISO 815 |
73°F, 22 hr | 15 | % |
|
158°F, 22 hr | 35 | % |
|
巴肖氏弹性 | 25 | % | ASTM D2632 |
玻璃转化温度 | -4.00 | °F | DMA |
维卡软化温度 | 239 | °F | ISO 306/A50, ASTM D1525 4 |
干燥温度 - 热风干燥机 | 199 到 219 | °F |
|
干燥时间 - 热风干燥机 | 2.0 | hr |
|
建议的最大水分含量 | 0.030 | % |
|
建议的最大回制料比例 | 20 | % |
|
料筒后部温度 | 374 到 410 | °F |
|
料筒中部温度 | 374 到 419 | °F |
|
料筒前部温度 | 392 到 428 | °F |
|
射嘴温度 | 401 到 437 | °F |
|
加工（熔体）温度 | 401 到 419 | °F |
|
模具温度 | 59 到 104 | °F |
|
注塑压力 | 6000 到 15000 | psi |
|
注射速度 | 慢到中等 |
|
|
背压 | < 200 | psi |
|
螺杆转速 | 40 到 80 | rpm |
|
垫层 | 0.125 | in |
|
Hold Pressure: 60 to 80% of Injection Pressure |
干燥温度 | 199 到 219 | °F |
|
干燥时间 | 2.0 | hr |
|
建议的最大回制料比例 | 20 | % |
|
料筒1区温度 | 356 到 392 | °F |
|
料筒3区温度 | 356 到 401 | °F |
|
料筒5区温度 | 356 到 410 | °F |
|
熔体温度 | 374 到 401 | °F |
|
口模温度 | 365 到 410 | °F |
|
如需科思创原厂物性表及相关文件，请联系我们工作人员，谢谢！