Desmopan® 9395AU
热塑性聚氨酯弹性体（聚醚）
Extrusion- and injection molding grade; with special UV stabilizers; very good hydrolysis and microbial resistance; good low-temperature flexibility; Application; Pneumatic hoses; Profiles; Cable sheathings; Injection molded engineering parts
密度 |
|
|
|
73°F | 1.15 | g/cm³ | ISO 1183 |
-- | 0.0415 | lb/in³ | ISO 1183 2 |
肖氏硬度 |
|
|
|
邵氏 A, 1 秒, 73°F | 95 |
| ISO 7619 |
邵氏 D, 1 秒, 73°F | 46 |
| ISO 7619 |
邵氏 A, 3 sec | 95 |
| ISO 868 2 |
邵氏 D, 15 sec | 46 |
| ISO 868 2 |
拉伸应力 3 |
|
| DIN 53504 |
断裂, 73°F | 7640 | psi |
|
10% 应变, 73°F | 943 | psi |
|
50% 应变, 73°F | 1650 | psi |
|
100% 应变, 73°F | 2000 | psi |
|
300% 应变, 73°F | 4350 | psi |
|
拉伸应变 3 (断裂, 73°F) | 440 | % | DIN 53504 |
Tensile Storage Modulus |
|
| ISO 6721 |
-4°F | 63817 | psi |
|
68°F | 15084 | psi |
|
140°F | 7977 | psi |
|
抗磨损性 4 | 30.0 | mm³ | ISO 4649 |
撕裂强度 5 (73°F) | 570 | lbf/in | ISO 34-1 |
压缩永久变形 |
|
| ISO 815 |
73°F, 72 hr | 22 | % |
|
158°F, 24 hr 4 | 55 | % |
|
158°F, 24 hr 6 | 43 | % |
|
干燥温度 | < 230 | °F |
|
加工（熔体）温度 | 410 到 446 | °F |
|
模具温度 | 68 到 104 | °F |
|
干燥温度 | < 230 | °F |
|
熔体温度 | 392 到 428 | °F |
|
如需科思创原厂物性表及相关文件，请联系我们工作人员，谢谢！