Desmopan® 9392A
热塑性聚氨酯弹性体
Extrusion- and injection molding grade; very good hydrolysis and microbial resistance; good low-temperature flexibility; Application; Hoses, non-reinforced; Cable sheathings; Profiles; Technical parts
密度 (73°F) | 1.15 | g/cm³ | ISO 1183 |
肖氏硬度 |
|
| ISO 7619 |
邵氏 A, 1 秒, 73°F | 92 |
|
|
邵氏 D, 1 秒, 73°F | 42 |
|
|
拉伸应力 2 |
|
| DIN 53504 |
断裂, 73°F | 7250 | psi |
|
100% 应变, 73°F | 1600 | psi |
|
300% 应变, 73°F | 4350 | psi |
|
拉伸应变 2 (断裂, 73°F) | 400 | % | DIN 53504 |
Tensile Storage Modulus |
|
| ISO 6721 |
-4°F | 102 | ksi |
|
68°F | 19.1 | ksi |
|
140°F | 10.3 | ksi |
|
Torsional Storage Modulus |
|
| ISO 6721 |
-4°F | 15084 | psi |
|
73°F | 3191 | psi |
|
158°F | 1885 | psi |
|
抗磨损性 3 | 20.0 | mm³ | ISO 4649 |
撕裂强度 4 (73°F) | 490 | lbf/in | ISO 34-1 |
压缩永久变形 |
|
| ISO 815 |
73°F, 72 hr | 20 | % |
|
158°F, 24 hr 3 | 55 | % |
|
158°F, 24 hr 5 | 37 | % |
|
Rebound Resilience | 32 | % | ISO 4662 |
干燥温度 | < 176 | °F |
|
加工（熔体）温度 | 410 到 446 | °F |
|
模具温度 | 68 到 104 | °F |
|
干燥温度 | < 176 | °F |
|
熔体温度 | 383 到 419 | °F |
|
如需科思创原厂物性表及相关文件，请联系我们工作人员，谢谢！