Desmopan® 9380AU
热塑性聚氨酯弹性体（聚醚）
Extrusion- and injection molding grade; very good hydrolysis and microbial resistance; good low-temperature flexibility; complies with VDE 0282-10; with special UV stabilizers; Application; Cable sheathings; Hoses, non-reinforced; Technical parts
密度 |
|
|
|
73°F | 1.11 | g/cm³ | ISO 1183 |
-- | 0.0401 | lb/in³ | ISO 1183 2 |
肖氏硬度 |
|
|
|
邵氏 A, 1 秒, 73°F | 80 |
| ISO 7619 |
邵氏 D, 1 秒, 73°F | 31 |
| ISO 7619 |
邵氏 A, 3 sec | 80 |
| ISO 868 2 |
邵氏 D, 15 sec | 31 |
| ISO 868 2 |
拉伸应力 3 |
|
| DIN 53504 |
断裂, 73°F | 5930 | psi |
|
10% 应变, 73°F | 203 | psi |
|
50% 应变, 73°F | 551 | psi |
|
100% 应变, 73°F | 740 | psi |
|
300% 应变, 73°F | 1290 | psi |
|
拉伸应变 3 (断裂, 73°F) | 630 | % | DIN 53504 |
Tensile Storage Modulus |
|
| ISO 6721 |
-4°F | 10588 | psi |
|
68°F | 5366 | psi |
|
140°F | 4351 | psi |
|
抗磨损性 4 | 20.0 | mm³ | ISO 4649 |
撕裂强度 5 (73°F) | 290 | lbf/in | ISO 34-1 |
压缩永久变形 |
|
| ISO 815 |
73°F, 72 hr | 25 | % |
|
158°F, 24 hr 4 | 42 | % |
|
Rebound Resilience | 50 | % | ISO 4662 |
干燥温度 | < 176 | °F |
|
加工（熔体）温度 | 401 到 437 | °F |
|
模具温度 | 68 到 104 | °F |
|
干燥温度 | < 176 | °F |
|
熔体温度 | 383 到 419 | °F |
|
如需科思创原厂物性表及相关文件，请联系我们工作人员，谢谢！