Desmopan® 487
热塑性聚氨酯弹性体（聚酯）
injection molding grade; grease and oil-resistant; low compression set; good heat resistance; short cycle times; Application; Automotive engineering; Roller coating; Seals, membranes; Damping elements
特性 | - 低的压缩变形性、快的成型周期、耐热性高、耐油性能、耐油脂性能
|
用途 | |
RoHS 合规性 | |
加工方法 | |
多点数据 | Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)
|
密度 (73°F) | 1.20 | g/cm³ | ISO 1183 |
肖氏硬度 |
|
| ISO 7619 |
邵氏 A, 1 秒, 73°F | 86 |
|
|
邵氏 D, 1 秒, 73°F | 33 |
|
|
拉伸应力 2 |
|
| DIN 53504 |
断裂, 73°F | 6060 | psi |
|
10% 应变, 73°F | 232 | psi |
|
50% 应变, 73°F | 653 | psi |
|
100% 应变, 73°F | 841 | psi |
|
300% 应变, 73°F | 2090 | psi |
|
拉伸应变 2 (断裂, 73°F) | 540 | % | DIN 53504 |
Tensile Storage Modulus |
|
| ISO 6721 |
-4°F | 26542 | psi |
|
68°F | 5221 | psi |
|
140°F | 3481 | psi |
|
抗磨损性 3 | 12.0 | mm³ | ISO 4649 |
撕裂强度 4 (73°F) | 480 | lbf/in | ISO 34-1 |
压缩永久变形 |
|
| ISO 815 |
73°F, 72 hr | 13 | % |
|
158°F, 24 hr 3 | 23 | % |
|
158°F, 24 hr 5 | 16 | % |
|
Rebound Resilience | 57 | % | ISO 4662 |
干燥温度 | < 176 | °F |
|
加工（熔体）温度 | 446 到 464 | °F |
|
模具温度 | 68 到 104 | °F |
|
如需科思创原厂物性表及相关文件，请联系我们工作人员，谢谢！