Radiflam® S RV250 FR 9054 GRI
聚酰胺6
PA6 flame retardant injection moulding grade, halogen and phosphorus free. 25% glass fiber reinforced. Grey colour.
Suitable for parts requiring fire retardancy along with medium stiffness and good mechanical resistance. Low smoke toxicity and optical density. Rated V-0 according to UL-94.
填料/增强材料 | |
添加剂 | |
特性 | |
RoHS 合规性 | |
外观 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.68 | -- | g/cm³ | ISO 1183 |
收缩率 3 |
|
|
| ISO 294-4 |
横向流量 | 0.60 | -- | % |
|
流量 | 0.30 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
饱和, 73°F, 0.0787 in | 2.5 | -- | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 1.1 | -- | % |
|
拉伸模量 | 2.22E+6 | 1.62E+6 | psi | ISO 527-2/1A/1 |
拉伸应力 (断裂) | 19600 | 14500 | psi | ISO 527-2/1A/5 |
拉伸应变 (断裂) | 1.7 | 1.8 | % | ISO 527-2/1A/5 |
弯曲模量 4 | 2.10E+6 | -- | psi | ISO 178 |
弯曲应力 4 | 29000 | -- | psi | ISO 178 |
简支梁缺口冲击强度 |
|
|
| ISO 179/1eA |
-22°F | 1.9 | -- | ft·lb/in² |
|
73°F | 2.1 | 3.1 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
|
| ISO 179/1eU |
-22°F | 12 | -- | ft·lb/in² |
|
73°F | 17 | 19 | ft·lb/in² |
|
热变形温度 (264 psi, 未退火) | 392 | -- | °F | ISO 75-2/Af |
维卡软化温度 | 401 | -- | °F | ISO 306/B50 |
熔融温度 5 | 428 | -- | °F | ISO 11357-3 |
导热系数 (73°F) | 4.9 | -- | Btu·in/hr/ft²/°F | ASTM E1461 |
表面电阻率 6 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
体积电阻率 6 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
漏电起痕指数 (解决方案 A) | 600 | -- | V | IEC 60112 |
燃烧速率 (0.118 in) | 0.0 | -- | in/min | ISO 3795 |
UL 阻燃等级 (0.06 in) | V-0 | -- |
| UL 94 |
灼热丝易燃指数 |
|
|
| IEC 60695-2-12 |
0.04 in | 1760 | -- | °F |
|
0.08 in | 1760 | -- | °F |
|
热灯丝点火温度 |
|
|
| IEC 60695-2-13 |
0.04 in | 1340 | -- | °F |
|
0.08 in | 1340 | -- | °F |
|
干燥温度 - 热风干燥机 | 176 | °F |
|
干燥时间 - 热风干燥机 | 2.0 到 4.0 | hr |
|
Dew Point - 热风干燥机 | -4 | °F |
|
建议的最大水分含量 | 0.10 | % |
|
加工（熔体）温度 | 500 到 554 | °F |
|
模具温度 | 176 到 194 | °F |
|
注射速度 | 中等偏快 |
|
|