Radiflam® A RV350 HF 100 NAT 4570
聚酰胺66
PA66 flame retardant injection moulding grade, halogen and red phosphorus free. 35% glass fiber reinforced. Natural colour.
Suitable for parts requiring fire retardancy along with high stiffness and good mechanical resistance. Good electrical insulating properties. Rated V-0 according to UL-94.
填料/增强材料 | |
添加剂 | |
特性 | - 刚性高、绝缘、良好的电气性能、磷含量低（到无）、无卤、阻燃性
|
RoHS 合规性 | |
外观 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.47 | -- | g/cm³ | ISO 1183 |
吸水率 |
|
|
| ISO 62 |
饱和, 73°F, 0.0787 in | 5.4 | -- | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 1.3 | -- | % |
|
拉伸模量 | 1.77E+6 | 1.46E+6 | psi | ISO 527-2/1A/1 |
拉伸应力 (断裂) | 23200 | 18100 | psi | ISO 527-2/1A/5 |
拉伸应变 (断裂) | 2.5 | 2.5 | % | ISO 527-2/1A/5 |
弯曲模量 3 | 1.70E+6 | 1.07E+6 | psi | ISO 178 |
弯曲应力 3 | 37000 | 27600 | psi | ISO 178 |
简支梁缺口冲击强度 |
|
|
| ISO 179/1eA |
-22°F | 5.7 | -- | ft·lb/in² |
|
73°F | 5.7 | 6.7 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
|
| ISO 179/1eU |
-22°F | 31 | -- | ft·lb/in² |
|
73°F | 33 | 33 | ft·lb/in² |
|
热变形温度 |
|
|
|
|
66 psi, 未退火 | 500 | -- | °F | ISO 75-2/Bf |
264 psi, 未退火 | 473 | -- | °F | ISO 75-2/Af |
维卡软化温度 | 482 | -- | °F | ISO 306/B50 |
熔融温度 4 | 500 | -- | °F | ISO 11357-3 |
表面电阻率 5 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
体积电阻率 5 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
漏电起痕指数 (解决方案 A) | 600 | -- | V | IEC 60112 |
UL 阻燃等级 (0.031 in) | V-0 | -- |
| UL 94 |
灼热丝易燃指数 |
|
|
| IEC 60695-2-12 |
0.04 in | 1760 | -- | °F |
|
0.08 in | 1760 | -- | °F |
|
热灯丝点火温度 |
|
|
| IEC 60695-2-13 |
0.04 in | 1380 | -- | °F |
|
0.08 in | 1380 | -- | °F |
|
可燃性 | 0 | -- | in/min | FMVSS 302 |
干燥温度 - 热风干燥机 | 176 | °F |
|
干燥时间 - 热风干燥机 | 2.0 到 4.0 | hr |
|
Dew Point - 热风干燥机 | -4 | °F |
|
建议的最大水分含量 | 0.10 | % |
|
加工（熔体）温度 | 536 到 572 | °F |
|
模具温度 | 176 到 212 | °F |
|
注射速度 | 中等偏快 |
|
|