TORZEN Marathon™ G3500XHL BK34
聚酰胺66
PA66 35% glass fiber reinforced injection molding grade with enhanced thermal resistance in contact with hot air. High improvement of mechanical properties retention versus standard polyamide 66 after heat ageing. Black colour.
Suitable for parts requiring high stiffness, good mechanical resistance and good heat ageing properties retention.
填料/增强材料 | |
特性 | - Good Heat Resistance、刚性高、良好的耐热老化性能
|
RoHS 合规性 | |
外观 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.42 | g/cm³ | ISO 1183 |
收缩率 |
|
| ISO 294-4 |
横向流量 | 0.90 到 1.1 | % |
|
流量 | 0.25 到 0.35 | % |
|
吸水率 |
|
| ISO 62 |
饱和, 73°F, 0.0787 in | 1.1 | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 1.7 | % |
|
拉伸模量 | 1.67E+6 | psi | ISO 527-2/1A/1 |
拉伸应力 (断裂) | 30500 | psi | ISO 527-2/1A/5 |
拉伸应变 (断裂) | 3.0 | % | ISO 527-2/1A/5 |
弯曲模量 2 | 1.52E+6 | psi | ISO 178 |
弯曲应力 2 | 46400 | psi | ISO 178 |
简支梁缺口冲击强度 |
|
| ISO 179/1eA |
-40°F | 4.8 | ft·lb/in² |
|
73°F | 5.7 | ft·lb/in² |
|
悬壁梁缺口冲击强度 (73°F) | 5.7 | ft·lb/in² | ISO 180/1A |
热变形温度 |
|
|
|
66 psi, 未退火 | 500 | °F | ISO 75-2/Bf |
264 psi, 未退火 | 482 | °F | ISO 75-2/Af |
熔融温度 3 | 504 | °F | ISO 11357-3 |
干燥温度 - 热风干燥机 | 176 | °F |
|
干燥时间 - 热风干燥机 | 2.0 到 4.0 | hr |
|
Dew Point - 热风干燥机 | -4 | °F |
|
建议的最大水分含量 | 0.15 | % |
|
加工（熔体）温度 | 536 到 572 | °F |
|
模具温度 | 176 到 212 | °F |
|
注射速度 | 中等偏快 |
|
|
如需兰蒂奇原厂物性表及相关文件，请联系我们工作人员，谢谢！