产品说明:

ACRYMID® TT50 is a highly heat distortion-resistant poly(n-methyl methacrylimide) (PMMI). Besides showing the properties common to all ACRYMID® molding compounds, such as
  • high heat deflection temperature under load,

  • excellent transmission and clarity,

  • very high strength and rigidity, as well as

  • good weather resistance.


ACRYMID® TT50 is special in that it is
  • listed by AMECA.


Application:
ACRYMID® molding compound is particularly suitable for injection molding of items meant for applications that involve high heat loads.


特性
  • High Light Transmission、刚性高、高强度、耐气候影响性能良好、耐热性高、清晰度高
用途
  • Lighting Applications、光纤电缆、镜头、汽车领域的应用
形式
  • 粒子

加工方法
  • 注射成型

物理性能
额定值
单位制
测试方法
密度
1.21
g/cm³
ISO 1183
熔融体积流量(MVR) (260°C/10.0 kg)
0.305
in³/10min
ISO 1133
机械性能
额定值
单位制
测试方法
拉伸模量
580000
psi
ISO 527-2/1
拉伸应力 (断裂)
11600
psi
ISO 527-2/5
拉伸应变 (断裂)
3.0
%
ISO 527-2/5
冲击性能
额定值
单位制
测试方法
简支梁无缺口冲击强度 (73°F)
9.5
ft·lb/in²
ISO 179/1eU
热性能
额定值
单位制
测试方法
热变形温度



66 psi, 未退火
284
°F
ISO 75-2/B
264 psi, 未退火
270
°F
ISO 75-2/A
玻璃转化温度
304
°F
IEC 10006
维卡软化温度
302
°F
ISO 306/B50
线形热膨胀系数 - 流动 (32 到 122°F)
2.9E-5
in/in/°F
ISO 11359-2
可燃性
额定值

测试方法
UL 阻燃等级 (0.06 in)
HB

IEC 707
Fire Rating
B2

DIN 4102
光学性能
额定值
单位制
测试方法
折射率
1.530

ISO 489
透射率
91.0
%
ISO 13468-2
注射
额定值
单位制

干燥温度
< 266
°F

干燥时间
2.0 到 3.0
hr

加工(熔体)温度
482 到 536
°F

模具温度
230
°F


如需德固赛原厂物性表及相关文件,请联系我们工作人员,谢谢!