VESTAKEEP® 2000 FC30
聚醚醚酮
Carbon fiber-reinforced, graphite and PTFE-filled polyether ether ketone
VESTAKEEP 2000 FC30 is a medium-viscosity, carbon fiber-reinforced, graphite and PTFEfilled
polyether ether ketone for injection molding. Parts made of this resin can be used for bearing bushing or gearbox parts, due to the self-lubricating effect.
The semi-crystalline polymer features superior mechanical, thermal, and chemical resistance. Parts made from VESTAKEEP 2000 FC30 are self-extinguishing.
VESTAKEEP 2000 FC30 can be processed by common injection-molding machines for thermoplastics.
We recommend a melt temperature between 370°C and 380°C during the injection molding process. If temperatures exceed 380°C, toxic gases can be released. Adequate ventilation and protective
equipment must be provided. The mold temperature should be within a range of 160°C to 200°C, preferably 180°C.
填料/增强材料 | |
添加剂 | |
特性 | |
用途 | |
形式 | |
加工方法 | |
密度 | 1.45 | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (380°C/5.0 kg) | 0.915 | in³/10min | ISO 1133 |
收缩率 2 |
|
| ISO 294-4 |
横向流量 : 356°F, 0.0787 in | 0.40 | % |
|
流量 : 356°F, 0.0787 in | 0.10 | % |
|
拉伸模量 | 1.67E+6 | psi | ISO 527-2 |
拉伸应力 (断裂) | 21000 | psi | ISO 527-2 |
拉伸应变 (断裂) | 2.0 | % | ISO 527-2 |
简支梁缺口冲击强度 |
|
| ISO 179/1eA |
-22°F, 完全断裂 | 2.4 | ft·lb/in² |
|
73°F, 完全断裂 | 2.9 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
| ISO 179/1eU |
-22°F, 完全断裂 | 19 | ft·lb/in² |
|
73°F, 完全断裂 | 19 | ft·lb/in² |
|
热变形温度 |
|
|
|
66 psi, 未退火 | 639 | °F | ISO 75-2/B |
264 psi, 未退火 | 608 | °F | ISO 75-2/A |
维卡软化温度 |
|
|
|
-- | 644 | °F | ISO 306/A |
-- | 635 | °F | ISO 306/B |
熔融温度 3 | 644 | °F | ISO 11357-3 |
线形热膨胀系数 - 流动 (73 到 131°F) | 1.1E-5 | in/in/°F | ISO 11359-2 |
表面电阻率 | 1.0E+5 | ohms | IEC 60093 |
体积电阻率 | 1.0E+7 | ohms·cm | IEC 60093 |
相对电容率 |
|
| IEC 60250 |
50 Hz | 6.10 |
|
|
1 MHz | 4.90 |
|
|
UL 阻燃等级 (0.06 in) | V-0 |
| UL 94 |
灼热丝易燃指数 (0.08 in) | 1760 | °F | IEC 60695-2-12 |
热灯丝点火温度 (0.08 in) | 1650 | °F | IEC 60695-2-13 |
加工（熔体）温度 | 698 到 716 | °F |
|
模具温度 | 320 到 392 | °F |
|
如需德固赛原厂物性表及相关文件，请联系我们工作人员，谢谢！