VESTAMID® HTplus M1000
聚二甲苯酰胺
Unmodified polyphthalamide for creating compounds for injection molding
VESTAMID HTplus M1000 is a neat resin for polyphthalamide (PPA) based compounds for injection molding.
This base resin is especially suitable for manufacturing parts subjected to high temperature.
密度 (73°F) | 1.20 | g/cm³ | ISO 1183 |
拉伸模量 | 508000 | psi | ISO 527-2 |
拉伸应力 (断裂) | 13100 | psi | ISO 527-2 |
拉伸应变 (断裂) | 3.0 | % | ISO 527-2 |
简支梁缺口冲击强度 |
|
| ISO 179/1eA |
-40°F, 完全断裂 | 1.9 | ft·lb/in² |
|
73°F, 完全断裂 | 3.3 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
| ISO 179/1eU |
-40°F, 完全断裂 | 19 | ft·lb/in² |
|
73°F, 完全断裂 | 24 | ft·lb/in² |
|
热变形温度 |
|
|
|
66 psi, 未退火 | 433 | °F | ISO 75-2/B |
264 psi, 未退火 | 259 | °F | ISO 75-2/A |
维卡软化温度 |
|
|
|
-- | 576 | °F | ISO 306/A |
-- | 473 | °F | ISO 306/B |
熔融温度 2 | 572 到 599 | °F | ISO 11357-3 |
如需德固赛原厂物性表及相关文件，请联系我们工作人员，谢谢！