RTP 2282 HF
聚醚醚酮
产品说明:
Warning: The status of this material is 'Commercial: Limited Issue'
The data for this material has not been recently verified.
Please contact RTP Company for current information prior to specifying this grade.
填料/增强材料 | |
特性 | |
RoHS 合规性 | |
外观 | |
形式 | |
加工方法 | |
密度 / 比重 | 1.36 |
| ASTM D792 |
收缩率 - 流动 (0.125 in) | 1.0E-3 | in/in | ASTM D955 |
吸水率 (24 hr, 73°F) | 0.17 | % | ASTM D570 |
拉伸模量 | 2.20E+6 | psi | ASTM D638 |
抗张强度 | 27000 | psi | ASTM D638 |
伸长率 (断裂) | 1.7 | % | ASTM D638 |
弯曲模量 | 1.50E+6 | psi | ASTM D790 |
弯曲强度 | 39000 | psi | ASTM D790 |
悬壁梁缺口冲击强度 (0.125 in) | 1.0 | ft·lb/in | ASTM D256 |
无缺口悬臂梁冲击 (0.125 in) | 8.0 | ft·lb/in | ASTM D4812 |
载荷下热变形温度 |
|
| ASTM D648 |
66 psi, 未退火 | 550 | °F |
|
264 psi, 未退火 | 550 | °F |
|
体积电阻率 | 1.0E+5 | ohms·cm | ASTM D257 |
UL 阻燃等级 | V-0 |
| UL 94 |
Mold Shrinkage, Linear-Flow, ASTM D955, 0.25in.: 1.5mil/in. |
干燥温度 | 300 | °F |
|
干燥时间 | 3.0 | hr |
|
建议的最大水分含量 | 0.10 | % |
|
建议的最大回制料比例 | 20 | % |
|
料筒后部温度 | 675 到 750 | °F |
|
料筒中部温度 | 675 到 750 | °F |
|
料筒前部温度 | 675 到 750 | °F |
|
模具温度 | 350 到 500 | °F |
|
注塑压力 | 10000 到 20000 | psi |
|
背压 | 50.0 到 100 | psi |
|
锁模力 | 5.0 到 8.0 | tons/in² |
|
如需安特普原厂物性表及相关文件，请联系我们工作人员，谢谢！