TECHNYL® A 217 BLACK 1N
聚酰胺66
产品说明:
TECHNYL® A 217 Black 1 N is an unreinforced polyamide 66, heat stabilized, standard viscosity, for injection moulding. This grade offers all the primary properties of unreinforced polyamide 66. In addition it has improved resistance to high temperature and it can be used for components which have to withstand mid term temperature stresses. This grade can also be vacuum metalized with very good surface quality and adhesion of the aluminum surface.
添加剂 | |
特性 | - Heat Stabilized - Inorganic，电镀，良好的流动性，脱模性能良好
|
用途 | |
机构评级 | - EC 1907/2006 (REACH)EN 45545NF F 16-101UL QMFZ2
|
RoHS 合规性 | |
外观 | |
形式 | |
加工方法 | |
多点数据 | |
树脂ID (ISO 1043) | |
密度 | 1.14 | -- | g/cm³ | ISO 1183/A |
收缩率 |
|
|
| ISO 294-4 |
横向流量 | 1.4 | -- | % |
|
流量 | 1.4 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
73°F, 24 hr | 1.3 | -- | % |
|
平衡, 73°F, 50% RH | 2.9 | -- | % |
|
拉伸模量 (73°F) | 508000 | 247000 | psi | ISO 527-2/1A |
抗张强度 |
|
|
|
|
屈服, 73°F | 12300 | -- | psi | ASTM D638 |
屈服, 73°F | 13800 | 8700 | psi | ISO 527-2/1A |
断裂, 73°F | 8700 | 6530 | psi | ISO 527-2/1A |
拉伸应变 |
|
|
|
|
屈服, 73°F | 4.5 | 10 | % | ISO 527-2 |
断裂, 73°F | 30 | -- | % | ASTM D638 |
断裂, 73°F | > 30 | > 150 | % | ISO 527-2 |
弯曲模量 |
|
|
|
|
73°F | 508000 | -- | psi | ASTM D790 |
73°F | 450000 | 210000 | psi | ISO 178 |
弯曲强度 |
|
|
|
|
73°F | 18100 | -- | psi | ASTM D790 |
73°F | 18900 | 11600 | psi | ISO 178 |
简支梁缺口冲击强度 (73°F) | 2.1 | 5.2 | ft·lb/in² | ISO 179/1eA |
简支梁无缺口冲击强度 (73°F) | 无断裂 | 无断裂 |
| ISO 179/1eU |
悬壁梁缺口冲击强度 |
|
|
|
|
73°F | 1.5 | -- | ft·lb/in | ASTM D256 |
73°F | 1.9 | 4.8 | ft·lb/in² | ISO 180 |
无缺口伊佐德冲击强度 (73°F) | 无断裂 | 无断裂 |
| ISO 180/1U |
载荷下热变形温度 |
|
|
|
|
66 psi, 未退火 | 428 | -- | °F | ASTM D648 |
66 psi, 未退火 | 410 | -- | °F | ISO 75-2/Bf |
264 psi, 未退火 | 167 | -- | °F | ASTM D648, ISO 75-2/Af |
熔融温度 | 504 | -- | °F | ISO 11357-3 |
表面电阻率 | 1.0E+15 | 1.0E+14 | ohms | IEC 60093 |
体积电阻率 | 1.0E+15 | 1.0E+16 | ohms·cm | IEC 60093 |
介电强度 (0.0787 in) | 640 | 560 | V/mil | IEC 60243-1 |
相对电容率 | 2.90 | 3.20 |
| IEC 60250 |
耗散因数 | 0.030 | 0.080 |
| IEC 60250 |
漏电起痕指数 |
|
|
| IEC 60112 |
解决方案 A | 600 | 600 | V |
|
解决方案 B | 450 | -- | V |
|
UL 阻燃等级 |
|
|
| UL 94 |
0.06 in | V-2 | -- |
|
|
0.13 in | V-2 | -- |
|
|
灼热丝易燃指数 |
|
|
| IEC 60695-2-12 |
0.031 in | 1200 | -- | °F |
|
0.06 in | 1200 | -- | °F |
|
热灯丝点火温度 (0.06 in) | 1200 | -- | °F | IEC 60695-2-13 |
极限氧指数 | 26 | -- | % | ISO 4589-2 |
French Fire Index | F2 | -- |
| NF F16-101 |
French Smoke Index | I3 | -- |
| NF F16-101 |
European Railways Certifications |
|
|
| EN 45545-2 |
R22 | HL2 | -- |
|
|
R23 | HL2 | -- |
|
|
干燥温度 | 176 | °F |
|
建议的最大水分含量 | 0.20 | % |
|
料筒后部温度 | 509 到 527 | °F |
|
料筒中部温度 | 518 到 536 | °F |
|
料筒前部温度 | 536 到 545 | °F |
|
模具温度 | 140 到 176 | °F |
|
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4h Injection Advice: |
如需索尔维（SOLVAY）原厂物性表及相关文件，请联系我们工作人员，谢谢！