VICTREX WG™ POLYMER 102
High performance thermoplastic material, PolyArylEtherKetone (PAEK), semi crystalline, granules for injection moulding, standard flow, reinforced with wear additives, colour black. WG102 does not contain polytetrafluoroethylene (PTFE) or other halogenated additives or talc.
Higher temperature tribological applications for high strength and stiffness. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.
Material Properties |
Physical | Nominal Value | Unit | Test Method |
Density (Crystalline) | 1.44 | g/cm³ | ISO 1183 |
Spiral Flow |
|
| Internal Method |
-- 1 | 8.50 | cm |
|
-- 2 | 36.0 | cm |
|
Molding Shrinkage 3 |
|
| ISO 294-4 |
Across Flow | 0.60 | % |
|
Flow | 0.10 | % |
|
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 19500 | MPa | ISO 527-1 |
Tensile Stress |
|
| ISO 527-2 |
Break, 23°C | 195 | MPa |
|
Break, 125°C | 130 | MPa |
|
Break, 175°C | 85.0 | MPa |
|
Break, 275°C | 55.0 | MPa |
|
Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
Flexural Modulus (23°C) | 17000 | MPa | ISO 178 |
Flexural Stress |
|
| ISO 178 |
23°C | 290 | MPa |
|
125°C | 220 | MPa |
|
175°C | 145 | MPa |
|
275°C | 75.0 | MPa |
|
Compressive Stress |
|
| ISO 604 |
23°C | 250 | MPa |
|
120°C | 175 | MPa |
|
200°C | 80.0 | MPa |
|
250°C | 55.0 | MPa |
|
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C) | 35.0 | kJ/m² | ISO 179/1U |
Notched Izod Impact Strength (23°C) | 5.3 | kJ/m² | ISO 180/A |
Unnotched Izod Impact Strength (23°C) | 40.0 | kJ/m² | ISO 180 |
Hardness | Nominal Value | Unit | Test Method |
Shore Hardness (Shore D, 23°C) | 86.0 |
| ISO 868 |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 367 | °C | ISO 75-2/Af |
Glass Transition Temperature |
|
| ISO 11357-2 |
Onset | 152 | °C |
|
Midpoint | 160 | °C |
|
Melting Temperature | 373 | °C | ISO 11357-3 |
CLTE - Flow |
|
| ISO 11359-2 |
< 143°C | 9 | ppm/K |
|
> 143°C | 10 | ppm/K |
|
CLTE - Average |
|
| ISO 11359-2 |
< 143°C | 35 | ppm/K |
|
> 143°C | 90 | ppm/K |
|
Thermal Conductivity |
|
| ISO 22007-4 |
23°C 4 | 1.3 | W/m/K |
|
23°C 5 | 2.2 | W/m/K |
|
Electrical | Nominal Value | Unit | Test Method |
Volume Resistivity 6 (23°C) | 1.0E+7 | ohms·cm | IEC 60093 |
Fill Analysis | Nominal Value | Unit | Test Method |
Melt Viscosity (400°C) | 575 | Pa·s | ISO 11443 |
如需 威格斯（VICTREX）原厂物性表及相关文件，请联系我司工作人员，谢谢！