VICTREX CT™ POLYMER 200
High performance thermoplastic PAEK polymer micro-granules for injection and compression moulding and extrusion. Suitable for dynamic sealing applications at very low temperatures. Colour: Green.
Material Properties |
Physical | Nominal Value | Unit | Test Method |
Density (Crystalline) | 1.40 | g/cm³ | ISO 1183 |
Spiral Flow 1 | 9.10 | cm | Internal Method |
Molding Shrinkage 2 |
|
| ISO 294-4 |
Across Flow | 1.5 | % |
|
Flow | 1.1 | % |
|
Mechanical | Nominal Value | Unit | Test Method |
Tensile Stress |
|
| ISO 527-2 |
Yield, -196°C | 140 | MPa |
|
Yield, 23°C | 75.0 | MPa |
|
Tensile Strain |
|
| ISO 527-2 |
Break, -196°C | 4.0 | % |
|
Break, 23°C | 25 | % |
|
Flexural Modulus |
|
| ISO 178 |
-196°C | 5000 | MPa |
|
23°C | 3300 | MPa |
|
Flexural Stress |
|
| ISO 178 |
-196°C | 359 | MPa |
|
23°C | 132 | MPa |
|
3.5% Strain, 23°C | 100 | MPa |
|
Compressive Modulus (-196°C) | 5400 | MPa | ISO 604 |
Compressive Stress (-196°C) | 250 | MPa | ISO 604 |
Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact Strength (23°C) | 7.5 | kJ/m² | ISO 180/A |
Hardness | Nominal Value | Unit | Test Method |
Shore Hardness (Shore D, 23°C) | 80.0 |
| ISO 868 |
Thermal | Nominal Value | Unit | Test Method |
Glass Transition Temperature |
|
| ISO 11357-2 |
Onset | 143 | °C |
|
Midpoint | 150 | °C |
|
Melting Temperature | 343 | °C | ISO 11357-3 |
CLTE - Average |
|
|
|
-165°C | 42 | ppm/K | DIN 51909 |
23°C | 48 | ppm/K | ISO 11359-2 |
Thermal Conductivity |
|
| ISO 22007-4 |
-165°C | 0.15 | W/m/K |
|
23°C | 0.25 | W/m/K |
|