Radilon® S 40EPT2808 333 NER
聚酰胺6
PA6 high viscosity extrusion grade. Low modulus, high flexibility and high impact strength, even at low temperatures. Black colour.
This material has been designed for extrusion of pipes. Typical application: convoluted fuel pipes for the automotive industry.
特性 | - High Flexibility、抗撞击性高、耐低温冲击、粘度高
|
用途 | |
RoHS 合规性 | |
外观 | |
加工方法 | |
树脂ID (ISO 1043) | |
拉伸模量 | 131000 | -- | psi | ISO 527-2/1A/1 |
拉伸应力 (屈服) | 5080 | -- | psi | ISO 527-2/1A/50 |
标称拉伸断裂应变 | > 100 | -- | % | ISO 527-2/1A/50 |
弯曲模量 2 | 79800 | -- | psi | ISO 178 |
弯曲应力 2 | 3630 | -- | psi | ISO 178 |
简支梁缺口冲击强度 (73°F) | 31 | -- | ft·lb/in² | ISO 179/1eA |
热变形温度 (264 psi, 未退火) | 122 | -- | °F | ISO 75-2/Af |
维卡软化温度 | 248 | -- | °F | ISO 306/B50 |
熔融温度 3 | 428 | -- | °F | ISO 11357-3 |
表面电阻率 4 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
体积电阻率 4 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
漏电起痕指数 (解决方案 A) | 600 | -- | V | IEC 60112 |
UL 阻燃等级 (0.031 in) | HB | -- |
| UL 94 |
可燃性 | < 1 | -- | in/min | FMVSS 302 |
干燥温度 - 热风干燥机 | 176 | °F |
|
干燥时间 - 热风干燥机 | 2.0 到 4.0 | hr |
|
Dew Point - 热风干燥机 | -4 | °F |
|
建议的最大水分含量 | 0.15 | % |
|
加工（熔体）温度 | 482 到 536 | °F |
|
模具温度 | 158 到 176 | °F |
|
注射速度 | 中等 |
|
|
熔体温度 | 464 到 518 | °F |
|
如需兰蒂奇原厂物性表及相关文件，请联系我们工作人员，谢谢！