Radilon® A RV300K 990 GRI
聚酰胺66
PA66 30% glass fiber reinforced injection moulding grade, low friction. Heat stabilized. Natural grey colour.
Suitable for parts requiring high stiffness, good mechanical resistance and low friction, along with good heat ageing properties retention. Particularly apt for components requiring improved wear resistance, such as gears, bearings, and cams.
ISO 1043 : PA66-T GF30
填料/增强材料 | |
添加剂 | |
特性 | - 低摩擦系数、刚性高、良好的耐热老化性能、耐磨损性良好、热稳定性
|
用途 | |
RoHS 合规性 | |
UL文件号 | |
外观 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.35 | -- | g/cm³ | ISO 1183 |
吸水率 |
|
|
| ISO 62 |
饱和, 73°F, 0.0787 in | 7.0 | -- | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 1.7 | -- | % |
|
拉伸模量 | 1.48E+6 | -- | psi | ISO 527-2/1A/1 |
拉伸应力 (断裂) | 25400 | -- | psi | ISO 527-2/1A/5 |
拉伸应变 (断裂) | 3.5 | -- | % | ISO 527-2/1A/5 |
弯曲模量 3 | 1.35E+6 | -- | psi | ISO 178 |
弯曲应力 3 | 37700 | -- | psi | ISO 178 |
简支梁无缺口冲击强度 (73°F) | 40 | -- | ft·lb/in² | ISO 179/1eU |
热变形温度 |
|
|
|
|
66 psi, 未退火 | 491 | -- | °F | ISO 75-2/Bf |
264 psi, 未退火 | 464 | -- | °F | ISO 75-2/Af |
维卡软化温度 | 464 | -- | °F | ISO 306/B50 |
熔融温度 4 | 500 | -- | °F | ISO 11357 |
表面电阻率 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
体积电阻率 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
漏电起痕指数 | 500 | -- | V | IEC 60112 |
燃烧速率 | 0.0 | -- | in/min | FMVSS 302 |
UL 阻燃等级 (0.031 in) | HB | -- |
| UL 94 |
灼热丝易燃指数 (0.08 in) | 1290 | -- | °F | IEC 60695-2-12 |
干燥温度 - 热风干燥机 | 176 | °F |
|
干燥时间 - 热风干燥机 | 2.0 到 4.0 | hr |
|
Dew Point - 热风干燥机 | < -4 | °F |
|
建议的最大水分含量 | 0.15 | % |
|
加工（熔体）温度 | 536 到 572 | °F |
|
模具温度 | 176 到 212 | °F |
|
注射速度 | 中等偏快 |
|
|