Radilon® A ERV1906LK 100 NAT
聚酰胺66
PA66 13% glass fiber reinforced injection moulding grade. Toughened, lubricated and heat stabilized. Natural colour.
Suitable for parts requiring improved impact strength along with enhanced stiffness.
A typical application are anti-vibration rings.
填料/增强材料 | |
添加剂 | |
特性 | |
RoHS 合规性 | |
外观 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.22 | -- | g/cm³ | ISO 1183 |
收缩率 2 |
|
|
| ISO 294-4 |
横向流量 | 0.80 | -- | % |
|
流量 | 0.40 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
饱和, 73°F, 0.0787 in | 7.5 | -- | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 1.9 | -- | % |
|
拉伸模量 | 725000 | 609000 | psi | ISO 527-2/1A/1 |
拉伸应力 |
|
|
|
|
屈服 | -- | 10900 | psi | ISO 527-2/1A/50 |
断裂 | 14500 | -- | psi | ISO 527-2/1A/5 |
拉伸应变 |
|
|
|
|
屈服 | -- | 8.0 | % | ISO 527-2/1A/50 |
断裂 | 4.0 | -- | % | ISO 527-2/1A/5 |
标称拉伸断裂应变 | -- | 17 | % | ISO 527-2/1A/50 |
弯曲模量 3 | 624000 | -- | psi | ISO 178 |
弯曲应力 3 | 21800 | -- | psi | ISO 178 |
简支梁缺口冲击强度 |
|
|
| ISO 179/1eA |
-22°F | 2.3 | 2.4 | ft·lb/in² |
|
73°F | 5.5 | 7.1 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
|
| ISO 179/1eU |
-22°F | 19 | 20 | ft·lb/in² |
|
73°F | 36 | 48 | ft·lb/in² |
|
热变形温度 |
|
|
|
|
66 psi, 未退火 | 446 | -- | °F | ISO 75-2/Bf |
264 psi, 未退火 | 347 | -- | °F | ISO 75-2/Af |
维卡软化温度 | 455 | -- | °F | ISO 306/B50 |
熔融温度 4 | 500 | -- | °F | ISO 11357-3 |
表面电阻率 5 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
体积电阻率 5 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
漏电起痕指数 (解决方案 A) | 550 | -- | V | IEC 60112 |
UL 阻燃等级 (0.031 in) | HB | -- |
| UL 94 |
灼热丝易燃指数 (0.08 in) | 1290 | -- | °F | IEC 60695-2-12 |
可燃性 | < 10.0 | -- | mm/min | FMVSS 302 |
干燥温度 - 热风干燥机 | 176 | °F |
|
干燥时间 - 热风干燥机 | 2.0 到 4.0 | hr |
|
Dew Point - 热风干燥机 | -4 | °F |
|
建议的最大水分含量 | 0.15 | % |
|
加工（熔体）温度 | 536 到 572 | °F |
|
模具温度 | 176 到 212 | °F |
|
注射速度 | 中等偏快 |
|
|
如需兰蒂奇原厂物性表及相关文件，请联系我们工作人员，谢谢！