Radilon® A CF300K 333 NER
聚酰胺66
PA66 30% carbon fiber reinforced injection moulding grade. Heat stabilized. Black colour.
Suitable for parts and components requiring very high mechanical properties: stiffness, dimensional stability, fatigue and creep resistance.
The presence of carbon fibers also provides higher electrical and thermal conductivity.
填料/增强材料 | |
添加剂 | |
特性 | - High Dimensional Stability、导电、导热、刚性高、良好的抗蠕变性、耐疲劳性能、热稳定性
|
RoHS 合规性 | |
外观 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.27 | -- | g/cm³ | ISO 1183 |
吸水率 |
|
|
| ISO 62 |
饱和, 73°F, 0.0787 in | 6.0 | -- | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 1.7 | -- | % |
|
拉伸模量 | 3.34E+6 | 2.10E+6 | psi | ISO 527-2/1A/1 |
拉伸应力 (断裂) | 37000 | 23200 | psi | ISO 527-2/1A/5 |
拉伸应变 (断裂) | 2.1 | 2.5 | % | ISO 527-2/1A/5 |
弯曲模量 2 | 2.89E+6 | -- | psi | ISO 178 |
弯曲应力 2 | 53700 | -- | psi | ISO 178 |
简支梁缺口冲击强度 |
|
|
| ISO 179/1eA |
-22°F | 2.4 | -- | ft·lb/in² |
|
73°F | 3.3 | 4.3 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
|
| ISO 179/1eU |
-22°F | 29 | -- | ft·lb/in² |
|
73°F | 33 | 40 | ft·lb/in² |
|
热变形温度 |
|
|
|
|
66 psi, 未退火 | 482 | -- | °F | ISO 75-2/Bf |
264 psi, 未退火 | 455 | -- | °F | ISO 75-2/Af |
维卡软化温度 | 464 | -- | °F | ISO 306/B50 |
熔融温度 3 | 500 | -- | °F | ISO 11357-3 |
表面电阻率 4 | 1.0E+3 | 1.0E+3 | ohms | IEC 60093 |
体积电阻率 4 | 1.0E+4 | 1.0E+4 | ohms·cm | IEC 60093 |
漏电起痕指数 (解决方案 A) | 150 | -- | V | IEC 60112 |
UL 阻燃等级 (0.031 in) | HB | -- |
| UL 94 |
灼热丝易燃指数 (0.08 in) | 1290 | -- | °F | IEC 60695-2-12 |
可燃性 | < 10.0 | -- | mm/min | FMVSS 302 |
干燥温度 - 热风干燥机 | 176 | °F |
|
干燥时间 - 热风干燥机 | 2.0 到 4.0 | hr |
|
Dew Point - 热风干燥机 | -4 | °F |
|
建议的最大水分含量 | 0.15 | % |
|
加工（熔体）温度 | 536 到 572 | °F |
|
模具温度 | 176 到 212 | °F |
|
注射速度 | 中等 |
|
|
如需兰蒂奇原厂物性表及相关文件，请联系我们工作人员，谢谢！