Radilon® D CF150W 333 NER 6410
聚酰胺610
PA610 15% carbon fiber reinforced injection moulding grade. Heat stabilized. Black colour.
Suitable for parts and components requiring high mechanical properties.
The presence of carbon fibers also provides higher electrical and thermal conductivity.
This grade is partially renewably-sourced (60% of base polymer by weight).
填料/增强材料 | |
添加剂 | |
特性 | |
RoHS 合规性 | |
外观 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.15 | -- | g/cm³ | ISO 1183 |
吸水率 |
|
|
| ISO 62 |
饱和, 73°F, 0.0787 in | 2.7 | -- | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 1.2 | -- | % |
|
拉伸模量 | 1.68E+6 | -- | psi | ISO 527-2/1A/1 |
拉伸应力 (断裂) | 26100 | -- | psi | ISO 527-2/1A/5 |
拉伸应变 (断裂) | 4.0 | -- | % | ISO 527-2/1A/5 |
弯曲模量 2 | 1.38E+6 | -- | psi | ISO 178 |
弯曲应力 2 | 35500 | -- | psi | ISO 178 |
简支梁无缺口冲击强度 (73°F) | 31 | -- | ft·lb/in² | ISO 179/1eU |
表面电阻率 4 | 1.0E+5 | 1.0E+4 | ohms | IEC 60093 |
体积电阻率 4 | 1.0E+15 | 1.0E+4 | ohms·cm | IEC 60093 |
UL 阻燃等级 (0.031 in) | HB | -- |
| UL 94 |
干燥温度 - 热风干燥机 | 176 | °F |
|
干燥时间 - 热风干燥机 | 2.0 到 4.0 | hr |
|
Dew Point - 热风干燥机 | -4 | °F |
|
建议的最大水分含量 | 0.15 | % |
|
加工（熔体）温度 | 464 到 536 | °F |
|
模具温度 | 176 到 194 | °F |
|
注射速度 | 快速 |
|
|