Radilon® D 40P50K 100 NAT 5526
聚酰胺610
PA610 flexible, high viscosity extrusion grade. Plasticized. Heat stabilized. Natural colour.
Suitable for extrusion of tubes and profiles. Typical application: air pressure pipes.
This grade is partially renewably-sourced (60% of base polymer by weight).
添加剂 | |
特性 | |
用途 | |
RoHS 合规性 | |
外观 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.10 | -- | g/cm³ | ISO 1183 |
吸水率 |
|
|
| ISO 62 |
饱和, 73°F, 0.0787 in | 2.5 | -- | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 1.1 | -- | % |
|
拉伸模量 | 125000 | 79800 | psi | ISO 527-2/1A/1 |
拉伸应力 |
|
|
|
|
屈服 | 5800 | 4350 | psi | ISO 527-2/1A/50 |
断裂 | 7690 | -- | psi | ISO 527-2/1A/5 |
拉伸应变 (屈服) | 55 | -- | % | ISO 527-2/1A/50 |
标称拉伸断裂应变 | 300 | > 100 | % | ISO 527-2/1A/50 |
弯曲模量 2 | 97200 | -- | psi | ISO 178 |
弯曲应力 2 | 4350 | -- | psi | ISO 178 |
简支梁缺口冲击强度 |
|
|
| ISO 179/1eA |
-22°F | 2.9 | -- | ft·lb/in² |
|
73°F | 9.5 | 17 | ft·lb/in² |
|
热变形温度 (264 psi, 未退火) | 122 | -- | °F | ISO 75-2/Af |
熔融温度 3 | 419 | -- | °F | ISO 11357-3 |
表面电阻率 4 | 1.0E+12 | -- | ohms | IEC 60093 |
体积电阻率 4 | 1.0E+15 | -- | ohms·cm | IEC 60093 |
干燥温度 - 热风干燥机 | 176 | °F |
|
干燥时间 - 热风干燥机 | 2.0 到 4.0 | hr |
|
Dew Point - 热风干燥机 | -4 | °F |
|
建议的最大水分含量 | 0.10 | % |
|
加工（熔体）温度 | 446 到 500 | °F |
|
模具温度 | 158 到 176 | °F |
|
注射速度 | 中等 |
|
|
熔体温度 | 446 到 482 | °F |
|