Radilon® D 40EP25ZW 7037 BLU 6556
聚酰胺610
PA610 flexible, high viscosity extrusion grade. Toughened and plasticized. Heat stabilized. Blue colour.
Suitable for extrusion of pipes, profiles and cable jackets. Good impact resistance also at low temperatures.
This grade is partially renewably-sourced (60% of base polymer by weight).
添加剂 | |
特性 | - 经增塑、抗撞击性良好、可更新资源、耐低温冲击、热稳定性、粘度高
|
用途 | |
RoHS 合规性 | |
外观 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.04 | -- | g/cm³ | ISO 1183 |
吸水率 |
|
|
| ISO 62 |
饱和, 73°F, 0.0787 in | 2.0 | -- | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 0.90 | -- | % |
|
拉伸模量 | 74000 | 50800 | psi | ISO 527-2/1A/1 |
拉伸应力 |
|
|
|
|
断裂 | 5220 | 4790 | psi | ISO 527-2/1A/5 |
100% 应变 | 4060 | 3340 | psi | ISO 527-2/1A/50 |
标称拉伸断裂应变 | 300 | 330 | % | ISO 527-2/1A/50 |
弯曲模量 2 | 65300 | 43500 | psi | ISO 178 |
弯曲应力 2 | 2470 | 1890 | psi | ISO 178 |
简支梁缺口冲击强度 |
|
|
| ISO 179/1eA |
-22°F | 26 | -- | ft·lb/in² |
|
73°F | 45 | 52 | ft·lb/in² |
|
热变形温度 |
|
|
|
|
66 psi, 未退火 | 212 | -- | °F | ISO 75-2/Bf |
264 psi, 未退火 | 122 | -- | °F | ISO 75-2/Af |
熔融温度 3 | 419 | -- | °F | ISO 11357-3 |
表面电阻率 4 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
体积电阻率 4 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
干燥温度 - 热风干燥机 | 176 | °F |
|
干燥时间 - 热风干燥机 | 2.0 到 4.0 | hr |
|
Dew Point - 热风干燥机 | -4 | °F |
|
建议的最大水分含量 | 0.10 | % |
|
加工（熔体）温度 | 446 到 500 | °F |
|
模具温度 | 158 到 176 | °F |
|
注射速度 | 中等 |
|
|
熔体温度 | 446 到 482 | °F |
|
如需兰蒂奇原厂物性表及相关文件，请联系我们工作人员，谢谢！