Stanyl® TW272B6
聚酰胺 46
产品说明:
30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified
Special Features:
Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
填料/增强材料 | |
添加剂 | |
特性 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.36 | -- | g/cm³ | ISO 1183 |
收缩率 |
|
|
| ISO 294-4 |
横向流量 | 0.60 | -- | % |
|
流量 | 0.30 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
饱和, 73°F | 8.1 | -- | % |
|
平衡, 73°F, 50% RH | 2.3 | -- | % |
|
粘数 | 150 | -- | cm³/g | ISO 307 |
拉伸模量 |
|
|
| ISO 527-2 |
-- | 3.48E+6 | 2.10E+6 | psi |
|
248°F | 1.81E+6 | -- | psi |
|
320°F | 1.60E+6 | -- | psi |
|
356°F | 1.52E+6 | -- | psi |
|
392°F | 1.45E+6 | -- | psi |
|
拉伸应力 |
|
|
| ISO 527-2 |
断裂 | 34800 | 23200 | psi |
|
断裂, 248°F | 18900 | -- | psi |
|
断裂, 320°F | 16000 | -- | psi |
|
断裂, 356°F | 14500 | -- | psi |
|
断裂, 392°F | 13100 | -- | psi |
|
拉伸应变 |
|
|
| ISO 527-2 |
断裂 | 1.6 | 3.5 | % |
|
断裂, 248°F | 3.1 | -- | % |
|
断裂, 320°F | 3.1 | -- | % |
|
断裂, 356°F | 3.1 | -- | % |
|
断裂, 392°F | 3.1 | -- | % |
|
简支梁缺口冲击强度 |
|
|
| ISO 179/1eA |
-22°F | 2.9 | 2.9 | ft·lb/in² |
|
73°F | 2.9 | 6.2 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
|
| ISO 179/1eU |
-22°F | 24 | 26 | ft·lb/in² |
|
73°F | 24 | 38 | ft·lb/in² |
|
热变形温度 (264 psi, 未退火) | 554 | -- | °F | ISO 75-2/A |
玻璃转化温度 3 | 167 | -- | °F | ISO 11357-2 |
熔融温度 3 | 563 | -- | °F | ISO 11357-3 |
线形热膨胀系数 |
|
|
| ISO 11359-2 |
流动 | 1.4E-5 | -- | in/in/°F |
|
横向 | 1.9E-5 | -- | in/in/°F |
|
干燥温度 | 176 | °F |
干燥时间 | 4.0 到 8.0 | hr |
料筒后部温度 | 536 到 608 | °F |
料筒中部温度 | 572 到 608 | °F |
料筒前部温度 | 572 到 608 | °F |
射嘴温度 | 572 到 608 | °F |
加工（熔体）温度 | 581 到 608 | °F |
模具温度 | 176 到 248 | °F |
注射速度 | 中等偏快 |
|
背压 | 290 到 1450 | psi |
螺杆压缩比 | 2.5:1.0 |
|