Stanyl® TW200B6
聚酰胺 46
产品说明:
30% Carbon Reinforced, Heat Stabilized, Lubricated
Special Features:
Used In:
Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
填料/增强材料 | |
添加剂 | |
特性 | |
用途 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.28 | -- | g/cm³ | ISO 1183 |
收缩率 |
|
|
| ISO 294-4 |
横向流量 | 0.90 | -- | % |
|
流量 | 0.20 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
饱和, 73°F | 9.5 | -- | % |
|
平衡, 73°F, 50% RH | 2.6 | -- | % |
|
拉伸模量 |
|
|
| ISO 527-2 |
-- | 3.48E+6 | -- | psi |
|
248°F | 1.45E+6 | -- | psi |
|
320°F | 1.28E+6 | -- | psi |
|
356°F | 1.20E+6 | -- | psi |
|
拉伸应力 |
|
|
| ISO 527-2 |
断裂 | 34800 | 21800 | psi |
|
断裂, 248°F | 18100 | -- | psi |
|
断裂, 320°F | 15200 | -- | psi |
|
断裂, 356°F | 13800 | -- | psi |
|
拉伸应变 |
|
|
| ISO 527-2 |
断裂 | 2.0 | 4.0 | % |
|
断裂, 248°F | 3.0 | -- | % |
|
断裂, 320°F | 3.0 | -- | % |
|
断裂, 356°F | 3.0 | -- | % |
|
弯曲模量 | 2.68E+6 | 1.33E+6 | psi | ISO 178 |
简支梁缺口冲击强度 |
|
|
| ISO 179/1eA |
-22°F | 3.1 | 3.1 | ft·lb/in² |
|
73°F | 3.8 | 6.7 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
|
| ISO 179/1eU |
-22°F | 24 | 24 | ft·lb/in² |
|
73°F | 29 | 36 | ft·lb/in² |
|
悬壁梁缺口冲击强度 |
|
|
| ISO 180/1A |
-40°F | 3.1 | 3.1 | ft·lb/in² |
|
73°F | 3.8 | 6.7 | ft·lb/in² |
|
干燥温度 | 176 | °F |
干燥时间 | 4.0 到 8.0 | hr |
料筒后部温度 | 536 到 608 | °F |
料筒中部温度 | 572 到 608 | °F |
料筒前部温度 | 572 到 608 | °F |
射嘴温度 | 572 到 608 | °F |
加工（熔体）温度 | 581 到 608 | °F |
模具温度 | 176 到 248 | °F |
注射速度 | 中等偏快 |
|
背压 | 290 到 1450 | psi |
螺杆压缩比 | 2.5:1.0 |
|
如需恩骅力（Envalior）原厂物性表及相关文件，请联系我司工作人员，谢谢！