Plexiglas® Satinice df33 zk6BR
聚甲基丙烯酸甲酯-丙烯酸
PLEXIGLAS® Satinice df33 zk6BR, based on PLEXIGLAS® Resist zk6BR, is an impact modified molding compound characterized by diffuse scattering of light.
Typical properties of impact modified PLEXIGLAS® molding compound are
Extruded parts from PLEXIGLAS® Satinice df33 zk6BR are characterized by the following special properties:
Application:
Used for (Co-) extruding profiles and sheets for the construction, furniture and automotive industry, but also for injection molding items for lighting engineering applications.
Examples:
applications that call for light diffusion combined with optimum transmission and velvet matt surface appearance is desired.
添加剂 | |
特性 | - High Light Diffusion、High Light Transmission、冲击改性、光泽中、抗撞击性高、耐气候影响性能良好、硬度高
|
用途 | - 家具、建筑应用领域、片材、汽车领域的应用、型材、照明漫射器
|
外观 | |
形式 | |
加工方法 | |
密度 | 1.16 | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (230°C/3.8 kg) | 0.0854 | in³/10min | ISO 1133 |
拉伸模量 | 290000 | psi | ISO 527-2/1 |
拉伸应力 (屈服) | 6530 | psi | ISO 527-2/50 |
拉伸应变 (屈服) | 4.0 | % | ISO 527-2/50 |
标称拉伸断裂应变 | 25 | % | ISO 527-2 |
简支梁无缺口冲击强度 (73°F) | 19 | ft·lb/in² | ISO 179/1eU |
热变形温度 |
|
|
|
66 psi, 未退火 | 210 | °F | ISO 75-2/B |
264 psi, 未退火 | 205 | °F | ISO 75-2/A |
维卡软化温度 | 210 | °F | ISO 306/B50 |
线形热膨胀系数 - 流动 (32 到 122°F) | 5.1E-5 | in/in/°F | ISO 11359-2 |
热灯丝点火温度 | 1290 | °F | IEC 60695-2-13 |
Half-Value Angle | 36.0 | ° | DIN 5036 |
Scattering Power | 0.490 |
| DIN 5036 |
干燥温度 | < 185 | °F |
|
干燥时间 | 2.0 到 3.0 | hr |
|
熔体温度 | 446 到 500 | °F |
|
口模温度 | 446 到 500 | °F |
|
如需德固赛原厂物性表及相关文件，请联系我们工作人员，谢谢！