Plexiglas® Hi-Gloss FT15 black 9V022
聚甲基丙烯酸甲酯-丙烯酸
PLEXIGLAS® Hi-Gloss FT15 black 9V022 is a special acrylic-based polymer.
With regard to its
PLEXIGLAS® Hi-Gloss FT15 9V022 shows comparable properties to those of PLEXIGLAS® standard molding compounds. In addition, PLEXIGLAS® Hi-Gloss FT15 9V022 offers the special benefit of a
Application:
PLEXIGLAS® Hi-Gloss FT15 9V022 is particularly suitable for injection molding technical components. Owing to ist superior brilliance, high-gloss (Class A) black surfaces can be obtained in.
Examples:
add-on automotive body parts
密度 | 1.19 | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (230°C/3.8 kg) | 0.275 | in³/10min | ISO 1133 |
拉伸模量 | 508000 | psi | ISO 527-2/1 |
拉伸应力 (断裂) | 7250 | psi | ISO 527-2/5 |
拉伸应变 (断裂) | 3.1 | % | ISO 527-2/5 |
简支梁无缺口冲击强度 (73°F) | 8.6 | ft·lb/in² | ISO 179/1eU |
热变形温度 |
|
|
|
66 psi, 未退火 | 225 | °F | ISO 75-2/B |
264 psi, 未退火 | 221 | °F | ISO 75-2/A |
玻璃转化温度 | 250 | °F | ISO 11357-2 |
维卡软化温度 | 239 | °F | ISO 306/B50 |
热灯丝点火温度 | 1250 | °F | IEC 60695-2-13 |
干燥温度 | 212 | °F |
|
干燥时间 | 4.0 到 6.0 | hr |
|
加工（熔体）温度 | 428 到 482 | °F |
|
模具温度 | 158 到 203 | °F |
|