Plexiglas® Hi-Gloss 8N black 9V022
聚甲基丙烯酸甲酯-丙烯酸
PLEXIGLAS® Hi-Gloss 8N black 9V022 is an amorphous thermoplastic molding compound (PMMA).
Typical properties of PLEXIGLAS® molding compounds are:
Special properties of PLEXIGLAS® Hi-Gloss 8N 9V022 are:
Application:
PLEXIGLAS® Hi-Gloss 8N black 9V022 is particularly suitable for injection molding technical components. Owing to its superior brilliance, high-gloss (Class A) black surfaces can be obtained.
Examples:
add-on automotive body parts
特性 | - 高光、高强度、良好的流动性、良好耐磨损性、耐气候影响性能良好、耐热性高、无定形的、硬度高
|
用途 | |
外观 | |
形式 | |
加工方法 | |
密度 | 1.19 | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (230°C/3.8 kg) | 0.183 | in³/10min | ISO 1133 |
拉伸模量 | 479000 | psi | ISO 527-2/1 |
拉伸应力 (断裂) | 11200 | psi | ISO 527-2/5 |
拉伸应变 (断裂) | 5.5 | % | ISO 527-2/5 |
简支梁无缺口冲击强度 (73°F) | 9.5 | ft·lb/in² | ISO 179/1eU |
热变形温度 |
|
|
|
66 psi, 未退火 | 217 | °F | ISO 75-2/B |
264 psi, 未退火 | 208 | °F | ISO 75-2/A |
玻璃转化温度 | 243 | °F | ISO 11357-2 |
维卡软化温度 | 226 | °F | ISO 306/B50 |
线形热膨胀系数 - 流动 (32 到 122°F) | 4.4E-5 | in/in/°F | ISO 11359-2 |
可燃性等级 (0.06 in) | HB |
| IEC 60695-11-10, -20 |
干燥温度 | < 208 | °F |
|
干燥时间 | 2.0 到 3.0 | hr |
|
加工（熔体）温度 | 428 到 500 | °F |
|
模具温度 | 140 到 194 | °F |
|